Preparation of β-belite using liquid alkali silicates

P. Koutník*

Unipetrol Centre for Research and Education, (Ústí nad Labem, Czech Republic)

*petr.koutnik@unicre.cz

 

ABSTRACT

The aim of this study is the preparation of β-belite by a solid-state reaction using powdered limestone, amorphous silica and liquid alkali silicates. The raw materials were blended, the mixtures were agglomerated and then burnt. The resulting samples were characterized by X-ray diffraction analysis and scanning electron microscopy. Free lime content in the β-belite samples was also determined. The effects of CaO/SiO2 ratio (1.6–2.1), burning temperature (800–1400 °C), utilization of different raw materials (silica fume, synthetic silica, potassium silicate, sodium silicate, potassium hydroxide) and burning time (0.5–16 h) on free lime content and mineralogical composition were investigated. The purest β-belite samples were prepared from a mixture of powdered limestone, silica fume and liquid potassium silicate with a ratio CaO/SiO2 = 2 by burning at temperatures between 1100 and 1300 °C for more than 2 h. Decreasing of the CaO/SiO2 ratio led to rankinite formation and lower a burning temperature led to the formation of wollastonite.

 

RESUMEN

Preparación de β-belita usando silicatos alcalinos líquidos. El objetivo de este estudio ha sido la preparación de β-belita por reacción en estado sólido usando caliza, sílice amorfa y silicatos alcalinos líquidos. Las materias primas se mezclaron y posteriormente, se aglomeraron y calcinaron. Los productos se caracterizaron mediante difracción de rayos X y microscopía electrónica de barrido. Se determinó el contenido de cal libre en la β-belita. Se ha estudiado el efecto de la relación CaO/SiO2 (1.6–2.1), temperatura de combustión (800–1400 °C), utilización de diferentes materias primas y el tiempo de combustión sobre el contenido de cal libre en el producto. La β-belita más pura se preparó a partir de la mezcla de piedra caliza en polvo, humo de sílice y silicato de potasio líquido con relación CaO/SiO2 = 2 a temperaturas entre 1100 y 1300 °C durante más de 2 horas. La disminución de la relación CaO/SiO2 produjo rankinita y una temperatura de combustión más baja produjo wollastonita.

 

Received 19 September 2016; Accepted 7 February 2017; Available on line 19 October 2017

Citation/Citar como: Koutník, P. (2017) Preparation of β-belite using liquid alkali silicates. Mater. Construcc. 67 [328], e140. http://dx.doi.org/10.3989/mc.2017.10816

KEYWORDS: Dicalcium silicate; Alkali; Silica Fume; Limestone; X-ray Diffraction (XRD)

PALABRAS CLAVE: Silicato bicálcico; Álcalis; Humo de sílice; Caliza; Difracción de rayos X (DRX)

ORCID ID: P. Koutník (http://orcid.org/0000-0002-3486-5577)

Copyright: © 2017 CSIC. This is an open-access article distributed under the terms of the Creative Commons Attribution License (CC BY) Spain 3.0.


 

CONTENT

1. INTRODUCTIONTOP

Cement production is associated with high energy consumption and CO2 emissions, therefore the cement industry is facing challenges to reduce them. One of the routes is the manufacturing of clinkers based on dicalcium silicate (C2S–belite). Belite formation generates reduced amounts of CO2 and also energy consumption is lower in comparison with tricalcium silicate (C3S – alite), the main component of Portland cement (1,2).

Dicalcium silicate exists in several polymorphic forms at ordinary pressures: α, α´H, α´L, β and γ (3). The γ form is thermodynamically stable at room temperature, but it has a lower degree of hydraulicity than the other forms. α, α´H, α´L and β forms are not stable in the pure state at room temperature (4,5). Chemical stabilization of these reactive belite forms can be carried out by the addition of many elements (K, Na, Fe, Mg, S, Ba) in various compounds, e.g. BaCl2, Na2SO4, NaF, K2CO3, Na2CO3, FeSO4 (3,5,611). Stabilization of the reactive belite structure was also achieved by the rapid cooling of clinker (3,8).

Although β-belite hydratation is much slower than that of alite, the later strength of the belite-rich and alite-rich cement pastes can be similar (3,12). Lower reactivity of belite is enhanced by the production of belite-rich cements, also containing other hydraulic phases and/or pozzolans. Belite sulfoaluminate cements and belite sulfoferroaluminate cements can contain whichever of the phases C2S, C12A7, CA, C2A3S, C4A3S, C4AF, CS, depending on clinker chemical composition (3,1216). Roman cements, key building material in the nineteenth century, are produced by burning of limestones rich in clay minerals, below their sintering point. Mineralogical compositions of Roman cements are variable, strongly depending on raw material composition. Roman cements typically contain phases C2S, quartz, free lime and amorphous aluminosilicates. Other phases can be CS, C3S2, C3A, C2AS and C4AF; C3S is excluded because of the low temperature during burning. Currently, Roman cements are especially manufactured for repairing historical monuments (1721).

Several methods of the preparation of belite cement or pure belite have been studied closely in laboratory scale. The most common process, corresponding to industrial production, involves the blending of powdered raw materials eventually followed by agglomeration, and final burning of the mixture (8,12,2225). Better homogenization can be achieved by dispergation of the raw materials in water or ethanol (5,911), especially under ultrasound treatment (6,26). A hydrothermal method for belite cement or pure belite preparation is more sophisticated and is also often applied. This method is based on hydrothermal synthesis of hydrated precursors (one or more items among C2SH, CSH, C3ASH4 etc.) and on their subsequent burning (1,7,9,2736). The described conditions of hydrothermal synthesis (temperature, pressure and time) are various; extending from ambient temperature and pressure and a long time (up to one month) (7) to high pressure and high temperature at short times (17 bar, 250°C, 4 h) (28). The hydrothermal process can be carried out not only in water but also in alkaline solutions (NaOH, KOH) (1,9,31,36). Other methods for pure belite preparation are based on a sol-gel process, using calcium nitrate tetrahydrate and silica sol to produce gel. The gel is dried and calcined (3743). Zeng (44) prepared belite by the co-precipitation of calcium silicate in CaCl2-Na2SiO3-NaOH solutions and subsequent calcination of the formed hydrated precursor.

The present work is focused on the preparation of β-belite by a solid-state reaction, using raw materials produced in high volumes in industrial scale: powdered limestone, amorphous silica and liquid alkali silicates (water glasses). These alkali silicates were used here for their ability to bind effectively powdered raw materials, and as a natural source of reactive SiO2 and of alkali ions, the latter having been reported as β-belite structure stabilizers. Systematic investigation was carried out to determine the influence of C/S ratio, reaction temperature and the sort of silica and alkali ions used on phase composition and free lime content.

2. MATERIALS AND METHODSTOP

2.1. MaterialsTOP

The raw materials used for dicalcium silicate preparation were partly powdered, such as synthetic silica (VP4; AV EKO-COLOR, s.r.o., Czech Republic), silica fume (České lupkové závody, a.s., Czech Republic) and limestone (Omyacarb 5VA; Omya), partly liquid, such as potassium silicate (Z. Ch. Rudniki S.A., Poland) and sodium silicate (Vodní sklo, a.s., Czech Republic).

The chemical compositions of powdered raw materials, determined by X-ray fluorescence, are presented in Table 1. The specific surface area obtained by the BET method, specific gravity and bulk density of powdered raw materials are shown in Table 2. The mineralogical compositions are given in XRD patterns in Figure 1. Particle size distributions are shown in Figure 2 and pore size distributions in Figure 3. The chemical compositions of liquid alkali silicates are presented in Table 3.

Table 1. Chemical composition (wt. %) of powdered raw materials
  LOIa SiO2 Al2O3 Fe2O3 CaO MgO K2O Na2O TiO2 P2O5 ZrO2 Cl SO3
Limestone 43.7 0.50 0.27 - 55.1 0.41 - - - - - - -
Silica fume 0.68 95.6 0.23 0.30 1.34 - - - - 0.44 1.14 - 0.11
Synthetic silica 4.23 92.3 0.22 0.06 0.16 2.14 0.01 0.47 0.06 - - 0.02 0.38
aLOI = Loss on ignition
Table 2. Physical properties of powdered raw materials
  BET (m2/g) Specific gravity (kg/m3) Bulk density (kg/m3)
Limestone 6.77 2658 787
Silica fume 15.32 2204 303
Synthetic silica 142.4 2111 174
Table 3. Chemical composition (wt. %) of liquid alkali silicates
  H2O SiO2 Al2O3 K2O Na2O
Potassium silicate 69.02 21.29 0.03 8.18 0.70
Sodium silicate 64.59 22.59 0.07 0.26 12.75

Figure 1. XRD patterns of powdered raw materials.

 

Figure 2. Particle size distributions of powdered raw materials.

 

Figure 3. Pore size distributions of powdered raw materials.

 

Analytical grade potassium hydroxide (Lachner) and distilled water were used to prepare a 25% KOH solution.

2.2. Analytical and testing methodsTOP

The chemical compositions of powdered raw materials were determined by X-ray fluorescence (BRUKER S8 Tiger).

A BRUKER D8 Advanced X-Ray diffraction system (XRD) equipped with BRUKER SSD 160 detector and operating with Cu-Kα radiation at 40 kV and 25 mA was used for analysis of raw materials and prepared dicalcium silicates. XRD scanning was taken at the 2θ = 0.02 step over an angular range from 5° to 70° with 1 s counting time.

A Mastersizer 2000 laser diffraction particle size analyser (MALVERN Instruments) was used to determine size distribution of powdered raw materials. Agglomerates were disrupted by ultrasound treatment.

Pore size distributions of powdered raw materials were determined using AutoPore 9510 mercury intrusion porosimeter (Micromeritics), which operates with pressures from 0.01 MPa to 414 MPa.

A gas sorption analyser Autosorb iQ from Quantachrome was used for the determination of specific surface area by the Brunauer-Emmett-Teller method (BET).

Free lime content in dicalcium silicate samples was determined by a glycerine-alcohol test.

The morphology of silica fume and synthetic silica was studied by a scanning electron microscope Mira 3 from (TESCAN).

An inductively coupled plasma optical emission spectrometer OPTIMA 8000 (Perkin Elmer) was used to determine the content of micro-elements and K/Na ratio in liquid alkali silicates. Total content of alkali metals (Na, K) and content of SiO2 in alkali silicates were determined by conventional acid-base titration methods; the reason for their application being higher accuracy at higher concentrations compared with other methods.

Specific gravity was determined by the pycnometric method.

2.3. ProcedureTOP

Ten mixtures M1–M10 were prepared by hand stirring in a vessel. Compositions of these mixtures, which are given in Table 4, were determined by calculation according to the required C/S ratios. The M8 mixture was a plastic material that was divided into amounts of about 20 g and dried at 120 °C. The others mixtures were compacted into tablets (diameter 40 mm, weight 20 g) under 20 kN using a hydraulic press. All agglomerated mixtures were burnt at a designed temperature in an electric muffle furnace for the required time, and then allowed to cool very slowly (overnight) inside the furnace. The heating rates were the maximum possible, which comprised the interval 8–12 °C/min. Twenty β-belite samples B1–B20 were obtained under the conditions shown in Table 5. Chemical compositions of the β-belite samples were found out by the calculation are given in Table 6.

Table 4. Compositions of raw materials mixtures (wt. %)
Raw material M1 M2 M3 M4 M5 M6 M7 M8 M9 M10
Limestone 58.73 59.73 60.65 61.49 62.27 62.99 61.54 62.53 69.49 68.37
Silica fume 17.27 16.27 15.35 14.51 13.73 13.01 - 13.48 21.36 21.02
Potassium silicate 24.00 24.00 24.00 24.00 24.00 24.00 24.00 - - -
Synthetic silica - - - - - - 14.46 - - -
Sodium silicate - - - - - - - 24.00 - -
H2O - - - - - - - - 9.14 -
KOH - 25% solution - - - - - - - - - 10.61
CaO/SiO2 (mol/mol) 1.60 1.70 1.80 1.90 2.00 2.10 2.00 2.00 2.00 2.00
Table 5. Conditions of β-belite preparation
Sample Mixture Agglomerates Burning temperature (°C) Burning time (h)
B1 M1 Tablets 1 100 8
B2 M2
B3 M3
B4 M4
B5 M5
B6 M6
B7 M5 Tablets 800 8
B8 950
B9 1 250
B10 1 300
B11 1 400
B12 M7 Tablets 1 100 8
B13 M8 Plastic material
B14 M9 Tablets
B15 M10 Tablets
B16 M5 Tablets 1 100 0.5
B17 1
B18 2
B19 4
B20 16
Table 6. Chemical composition (wt. %) of β-belite samples
Sample SiO2 Al2O3 Fe2O3 CaO MgO K2O Na2O P2O5 ZrO2 TiO2 CaO/SiO2 (mol/mol)
B1 38.08 0.34 0.09 56.85 0.42 3.42 0.29 0.13 0.34 - 1.60
B2 36.70 0.34 0.09 58.22 0.43 3.45 0.30 0.13 0.32 - 1.70
B3 35.41 0.34 0.08 59.50 0.44 3.47 0.30 0.12 0.31 - 1.80
B4 34.22 0.34 0.08 60.68 0.45 3.50 0.30 0.11 0.29 - 1.90
B5, B7–B11, B16–B20 33.10 0.35 0.07 61.79 0.46 3.52 0.30 0.11 0.28 - 2.00
B6 32.06 0.35 0.07 62.83 0.47 3.54 0.30 0.10 0.26 - 2.10
B12 32.99 0.35 0.02 61.56 1.00 3.56 0.42 - - 0.01 2.00
B13 32.53 0.34 0.07 60.74 0.45 0.11 5.37 0.10 0.27 - 2.00
B14 34.34 0.38 0.11 64.10 0.47 - - 0.16 0.40 - 2.00
B15 33.13 0.37 0.10 61.85 0.46 3.52 - 0.15 0.39 - 2.00

3. RESULTS AND DISCUSSIONTOP

3.1. Effect of CaO/SiO2 ratioTOP

All the samples B1–B6 with C/S ratio from 1.6 to 2.1 were white. Figure 4 shows their XRD patterns. The sample B5 (C/S = 2) contained mostly β-belite (larnite, ICDD 330302) and a small amount of lime (ICDD 821690). Sample B4 (C/S = 1.9) also included C3S2 (rankinite, ICDD 701138), whose content increased (while β-belite content decreases) with decreasing C/S ratio. The rise of the C/S ratio above 2 led to the increase in lime content.

Figure 4. XRD patterns of samples B1–B6 with different CaO/SiO2 ratio.

 

Free lime assessments (Figure 5) agreed with the results of XRD analysis described above. Free lime content was lower than 1 % up to C/S = 1.8; further increase of C/S ratio led to increasing free lime content. When the C/S ratio was 2, which is the stoichiometric ratio of these components in β-belite (sample B5), free lime content was 4.19 %, which means that approximately 93 % of CaO was bound.

Figure 5. Effect of CaO/SiO2 ratio on the free lime content.

 

3.2. Effect of burning temperatureTOP

The samples B5, B7, B8 were white in colour, while samples B9, B10 were light green. The sample B11 was amorphous green glass, obviously because of the applied temperature 1400 °C, which was higher than the melting point of mixture M5. The development of phase composition with burning temperature is shown in Figure 8. β-belite was present in all the samples burnt at temperatures from 800 °C to 1300 °C; its content rose up to 1100 °C, then held at 1300 °C. Another form of dicalcium silicate (ICDD 310297) was formed above 1250 °C. The sample B8, burnt at 950 °C also contained wollastonite (ICDD 431460) and probably pseudowollastonite (ICDD 896463), while the sample B7 burnt at 800 °C did not. β-belite is thus formed either by direct reaction of two molecules of CaO with an SiO2 molecule (sample B7) or by reacting one molecule CaO with CaSiO3 (wollastonite, sample B8), which is under certain conditions an intermediate of β-belite formation. Both of these mechanisms of β-belite formation were described (22,44) and the presence of wollastonite in the samples of β-belite or belite cements was documented (9, 22, 28, 44). The XRD patterns (Figure 6) did not present any α-belite and γ-belite peaks.

Figure 6. XRD patterns of samples B5 and B7–B11 with different burning temperatures.

 

The effect of burning temperature on the free lime content is shown graphically in Figure 7. Free lime rapidly diminished to the value 4.19 % up to the temperature 1100 °C. Further temperature increase brought about only moderate decrease in the free lime content.

Figure 7. Effect of burning temperature on free lime content.

 

Typical morphologies of the samples prepared at different temperatures are shown in Figures 810.

Figure 8. Morphology of sample B8 treated at 950 °C.

 

Figure 9. Morphology of sample B5 treated at 1 100.

 

Figure 10. Morphology of sample B11 treated at 1 400 °C.

 

The samples B7 and B8 are not homogenous. Spherical particles of silica fume are clearly visible in Figure 8. SEM morphologies of the samples B5, B9 and B10 are similar – materials are homogenous and particles are sintered (Figure 9). Figure 15 shows a glassy surface (sample B8), which was formed at temperatures exceeding the melting point of the mixture M5.

3.3. Effect of raw materialsTOP

The samples B5 and B12–B15 were prepared from various mixtures of raw materials, but the C/S ratio and the calcination procedure were kept the same. XRD patterns of these samples and the results of free lime determination, compared in Figure 11 and Figure 12 show differences in free lime content. The color of the sample B13 was light green, sample B14 was brownish and the rest of the samples were white.

Figure 11. XRD patterns of samples B5 and B12–B15 prepared from different raw materials (LS - limestone, SF - silica fume, SS - synthetic silica, KS - potassium silicate, NaS - sodium silicate, KOH - potassium hydroxide).

 

Figure 12. Effect of different raw materials utilisation on the free lime content.

 

The sample B5, prepared from a mixture of limestone, silica fume and potassium silicate had the lowest content of free lime. The replacement of potassium silicate with sodium silicate (B13) or potassium hydroxide (B15) led to a slight increase in free lime content. A significantly higher increase was caused by the replacement of silica fume with synthetic silica (B12). The highest lime content in the sample B14 demonstrates a significant influence of alkaline ions on the solid-state reaction rate. X-ray diffraction patterns are consistent with the results of free lime determination. All samples contained β-belite. The samples B15, B12 and B14 contained lime, the amounts of which increased respectively. The sample B13 probably contained sodium calcium silicate (ICDD 731726) and the sample B14 cristobalite (ICDD 391425). The diffraction pattern of the sample B12 explains why it contains more free lime than the sample B5, although synthetic silica has significantly higher specific surface area than silica fume (Table 2). The presence of rankinite in the sample of B12 indicates a local excess of SiO2 (see Figure 4). The reason for a higher content of free lime in the sample B12 is thus sample inhomogeneity rather than low reactivity of synthetic silica. Synthetic silica is less miscible with other components of the mixture compared to silica fume, due to considerably lower bulk density (Table 2).

3.4. Effect of burning timeTOP

The samples B5 and B16–B20 were prepared from the same mixture M5 (C/S = 2) by burning at 1 100 °C for various times (0.5–16 h). All of these samples were white. The influence of burning time on mineralogical composition and free lime content are shown in Figure 13 and Figure 14. All samples contained predominantly β-belite. The presence of lime and rankinite was clearly visible in the diffraction patterns of samples burned for less than 4 hours. The results of free lime content determination agreed with the results of XRD analysis. Free lime content rapidly decreased within the time of calcination 2 h to 4.80 %. Further prolongation of burning time did not change free lime content significantly. The presence of free lime residues in all samples indicates that the cause was not an excess of lime in the mixture (see Figure 5), neither slow reaction rate (see Figure 7 and Figure 14), but only inhomogeneities in the mixture of raw materials.

Figure 13. XRD patterns of samples B5 and B16–B20 with different burning time.

 

Figure 14. Effect of burning time on free lime content.

 

4. CONCLUSIONSTOP

β-belite with low content of free lime (below 5 %) was prepared by burning a mixture of powdered limestone, silica fume and liquid potassium silicate (water glass) with a ratio C/S = 2 and K2O content about 3,5 % at temperatures from 1 100 to 1 300 °C for more than 2 h. Increasing C/S ratio above 2 led to the an increase in free lime content. Rankinite was formed at a C/S ratio under 2; its content increased (while β-belite content decreases) with decreasing C/S ratio. A decrease in the burning temperature to 950 °C resulted in an increase in free lime content and formation of wollastonite – an intermediate of β-belite formation. Liquid potassium silicate in the reaction mixture was replaced with liquid sodium silicate or potassium hydroxide, without substantial deterioration in β-belite purity. The replacement of silica fume with synthetic silica with a low bulk density did not prove as expected because of low miscibility with other raw materials.

The described procedure for β-belite preparation is very simple and uses raw materials produced in large volumes. Therefore, it indicates high potential for industrial application, especially if impurity content is reduced by optimizing the amount of alkali metal in the reaction mixture.

 

ACKNOWLEDGMENTSTOP

The author thanks Karol Bayer (Faculty of Restoration, University of Pardubice) for providing SEM pictures.

The publication is a result of the project Development of the UniCRE Centre (project code LO1606) which was financially supported by the Ministry of Education, Youth and Sports of the Czech Republic under the National Sustainability Programme I.

 

REFERENCESTOP


1. Gartner, E. (2004) Industrially interesting approaches to “low-CO2” cements. Cem. Concr. Res. 34 (9), 1489–1498. http://dx.doi.org/10.1016/j.cemconres.2004.01.021
2. Schneider, M.; Romer, M.; Tschudin ,M.; Bolio, H. (2011) Sustainable cement production—present and future. Cem. Concr. Res. 41 (7), 642–650. http://dx.doi.org/10.1016/j.cemconres.2011.03.019
3. Chatterjee, A.K. (1996) High belite cements—Present status and future technological options: Part I. Cem. Concr. Res. 26 (8), 1213–1225. http://dx.doi.org/10.1016/0008-8846(96)00099-3
4. Bensted, J. (1978) Gamma-dicalcium silicate and its hydraulicity. Cem. Concr. Res. 8 (1), 73–76. http://dx.doi.org/10.1016/0008-8846(78)90059-5
5. Kriskova, L.; Pontikes ,Y.; Zhang, F.; Cizer, Ö.; Jones, P.T.; Van Balen ,K.; Blanpain, B. (2014) Influence of mechanical and chemical activation on the hydraulic properties of gamma dicalcium silicate. Cem. Concr. Res. 55, 59–68. http://dx.doi.org/10.1016/j.cemconres.2013.10.004
6. Rodrigues, F.A. (2003) Synthesis of chemically and structurally modified dicalcium silicate. Cem. Concr. Res. 33 (6), 823–827. http://dx.doi.org/10.1016/S0008-8846(02)01065-7.
7. Kurdowski, W.; Duszak, S.; Trybalska, B. (1997) Belite produced by means of low-temperature synthesis. Cem. Concr. Res. 27 (1), 51–62. http://dx.doi.org/10.1016/S0008-8846(96)00198-6
8. Kacimi, L.; Simon-Masseron ,A.; Salem, S.; Ghomari, A.; Derriche, Z. (2009) Synthesis of belite cement clinker of high hydraulic reactivity. Cem. Concr. Res. 39 (7), 559–565. http://dx.doi.org/10.1016/j.cemconres.2009.02.004
9. Pimraksa, K.; Hanjitsuwan, S.; Chindaprasirt, P. (2009) Synthesis of belite cement from lignite fly ash. Ceram. Int. 35 (6), 2415–2425. http://dx.doi.org/10.1016/j.ceramint.2009.02.006
10. Morsli, K.; De la Torre, A.G.; Cuberos, A.J.M.; Zahir, M.; Aranda, M.A.G. (2009) Preparation and characterization of alkali-activated white belite cements. Mater. Construcc. 59 (294), 19–29. http://dx.doi.org/10.3989/mc.2009.44307
11. Morsli, K.; De la Torre, A.G.; Stöber, S.; Cuberos, A.J.M.; Zahir, M.; Aranda, M.A.G. (2007) Quantitative Phase Analysis of Laboratory-Active Belite Clinkers by Synchrotron Powder Diffraction. J. Am. Ceram. Soc. 90 (10), 3205–3212. http://dx.doi.org/10.1111/j.1551-2916.2007.01870.x
12. Chen, Y.L.; Lin, Ch.J.; Ko, M.S.; Lai ,Y.Ch.; Chang, J.E. (2011) Characterization of mortars from belite-rich clinkers produced from inorganic waste. Cem. Concr. Comp. 33 (2), 261–266. http://dx.doi.org/10.1016/j.cemconcomp.2010.10.012
13. Zivica, V. (2000) Properties of blended sulfoaluminate belite cement. Constr. Build. Mater. 14 (8), 433–437. http://dx.doi.org/10.1016/S0950-0618(00)00050-7
14. Glasser, F.P.; Zhang, L. (2001) High-performance cement matrices based on calcium sulfoaluminate–belite compositions. Cem. Concr. Res. 31 (12), 1881–1886. http://dx.doi.org/10.1016/S0008-8846(01)00649-4
15. Strigac J.; Palou M. T.; Kristin J.; Majling J. (2000) Morphology and chemical composition of minerals inside the phase assemblage C-C2S-C4A3 S -C4AF-CS relevant to sulphoaluminate belite cements. Ceramics-Silikáty 44 (1), 26–34.
16. Martín-Sedeno, M.C.; Cuberos ,A.J.M.; De la Torre, A.G.; Álvarez-Pinazo, G.; Ordónez, L.M.; Gateshki, M.; Aranda, M.A.G. (2010) Aluminum-rich belite sulfoaluminate cements: Clinkering and early age hydration. Cem. Concr. Res. 40 (3), 359–369. http://dx.doi.org/10.1016/j.cemconres.2009.11.003
17. Tišlova, R.; Kozłowska, A.; Kozłowski, R.; Hughes, D. (2009) Porosity and specific surface area of Roman cement pastes. Cem. Concr. Res. 39 (10), 950–956. http://dx.doi.org/10.1016/j.cemconres.2009.06.020
18. Hughes, D.C.; Jaglin, D.; Kozłowski, R.; Mucha, D. (2009) Roman cements — Belite cements calcined at low temperature. Cem. Concr. Res. 39 (2), 77–89. http://dx.doi.org/10.1016/j.cemconres.2008.11.010
19. Gosselin, C.; Verges-Belmin, V.; Royer, A.; Martinet, G. (2009) Natural cement and monumental restoration. Mater. Struct. 42 (6), 749–763. http://dx.doi.org/10.1617/s11527-008-9421-7
20. Starinieri, V.; Hughes ,D.C.; Gosselin, C.; Wilk, D.; Bayer, K. (2013) Pre-hydration as a technique for the retardation of Roman cement mortars. Cem. Concr. Res. 46, 1–13. http://dx.doi.org/10.1016/j.cemconres.2013.01.004
21. Weber, J.; Gadermayr, N.; Kozłowski, R.; Mucha, D.; Hughes, D.; Jaglin, D.; Schwarz, W. (2007) Microstructure and mineral composition of Roman cements produced at defined calcination conditions. Mater. Char. 58 (11–12), 1217–1228. http://dx.doi.org/10.1016/j.matchar.2007.04.025
22. El-Didamony, H.; Khalil, Kh.A.; Ahmed, I.A.; Heikal, M. (2012) Preparation of β-dicalcium silicate (β-C2S) and calcium sulfoaluminate (C3A3 CS) phases using non-traditional nano-materials. Constr. Build. Mater. 35 77–83. http://dx.doi.org/10.1016/j.conbuildmat.2012.02.064
23. Ozturk, A.; Suyadal, Y.; Oguz, H. (2000) The formation of belite phase by using phosphogypsum and oil shale. Cem. Concr. Res. 30 (6), 967–971. http://dx.doi.org/10.1016/S0008-8846(00)00262-3
24. Staněk, T.; Sulovsky, P. (2015) Active low-energy belite cement. Cem. Concr. Res. 68, 203–210. http://dx.doi.org/10.1016/j.cemconres.2014.11.004
25. Gies, A.; Knofel ,D. (1986) Influence of alkalies on the composition of belite-rich cement clinkers and the technological properties of the resulting cements. Cem. Concr. Res. 16 (3), 411–422. http://dx.doi.org/10.1016/0008-8846(86)90117-1
26. Rodrigues, F.A. (2003) Low-temperature synthesis of cements from rice hull ash. Cem. Concr. Res. 33 (10), 1525–1529. http://dx.doi.org/10.1016/S0008-8846(03)00104-2
27. Mazouzi, W.; Kacimi, L.; Cyr M.; Clastres P. (2014) Properties of low temperature belite cements made from aluminosilicate wastes by hydrothermal method. Cem. Concr. Comp. 53, 170–177. http://dx.doi.org/10.1016/j.cemconcomp.2014.07.001
28. Maheswaran, S.; Kalaiselvam, S.; Saravana Karthikeyan, S.K.S.; Kokila, C.; Palani, G.S. (2016) β-Belite cements (β-dicalcium silicate) obtained from calcined lime sludge and silica fume. Cem. Concr. Comp. 66, 57–65. http://dx.doi.org/10.1016/j.cemconcomp.2015.11.008
29. Campillo, I.; Guerrero, A.; Dolado, J.S.; Porro, A.; Ibáñez, J.A.;Goñi, S. (2007) Improvement of initial mechanical strength by nanoalumina in belite cements. Materials Letters 61 (8–9), 1889–1892. http://dx.doi.org/10.1016/j.matlet.2006.07.150
30. Guerrero, A.; Goñi, S.; Macias, A.; Luxan, M.P. (2000) Effect of the starting fly ash on the microstructure and mechanical properties of fly ash–belite cement mortars. Cem. Concr. Res. 30 (4), 553–559. http://dx.doi.org/10.1016/S0008-8846(00)00198-8
31. Kacimi ,L.; Cyr, M.; Clastres, P. (2010) Synthesis of α′L-C2S cement from fly-ash using the hydrothermal method at low temperature and atmospheric pressure. J. Hazard. Mater. 181 (1–3), 593–601. http://dx.doi.org/10.1016/j.jhazmat.2010.05.054
32. Singh, N.B. (2006) Hydrothermal synthesis of β-dicalcium silicate (β-Ca2SiO4). Progress in crystal growth and characterization of materials 52 (1–2) 77–83. http://dx.doi.org/10.1016/j.pcrysgrow.2006.03.011
33. Link, T.; Bellmann ,F.; Ludwig, H.M.; Ben Haha, M. (2015) Reactivity and phase composition of Ca2SiO4 binders made by annealing of alpha-dicalcium silicate hydrate. Cem. Concr. Res. 67, 131–137. http://dx.doi.org/10.1016/j.cemconres.2014.08.009
34. Guerrero ,A.; Goñi, S.; Macias, A. (2000) Durability of new fly ash–belite cement mortars in sulfated and chloride medium. Cem. Concr. Res. 30 (8), 1231–1238. http://dx.doi.org/10.1016/S0008-8846(00)00313-6
35. Guerrero, A.; Goñi, S.; Macias, A.; Luxan, M.P. (1999) Hydraulic activity and microstructural characterization of new fly ash–belite cements synthesized at different temperatures. J. Mater. Res. 14 (6), 2680–2687. http://dx.doi.org/10.1557/JMR.1999.0359
36. Garbev, K.; Beuchle, G.; Schweike, U.; Merz, D.; Dregert, O.; Stemmermann P. (2014) Preparation of a Novel Cementitious Material from Hydrothermally Synthesized C-S-H Phases. J. Am. Ceram. Soc. 97 (7), 2298–2307. http://dx.doi.org/10.1111/jace.12920
37. Gou, Z,.; Chang, J. (2004) Synthesis and in vitro bioactivity of dicalcium silicate powders. J. Eur. Ceram. Soc. 24 (1), 93–99. http://dx.doi.org/10.1016/S0955-2219(03)00320-0
38. Stephan, D.; Wilhelm, P. (2004) Synthesis of Pure Cementitious Phases by Sol-Gel Process as Precursor. Z. Anorg. Allg. Chem. 630 (10), 1477–1483. http://dx.doi.org/10.1002/zaac.200400090
39. Gou, Z.; Chang, J.; Zhai, W.; Wang, J. (2005) Study on the Self-Setting Property and the In Vitro Bioactivity of β-Ca2SiO4. J. Biomed. Mater. Res. B Appl. Biomater. 73 (2), 244–251. http://dx.doi.org/10.1002/jbm.b.30203
40. Chrysafi, R.; Perraki, Th.; Kakali, G. (2007) Sol–gel preparation of 2CaO·SiO2. J. Eur. Ceram. Soc. 27 (2–3), 1707–1710. http://dx.doi.org/10.1016/j.jeurceramsoc.2006.05.004
41. Nettleship, I.; Shull, J.L.; Kriven, W. M. (1993) Chemical preparation and phase stability of Ca2SiO4 and Sr2SiO4 powders. J. Eur. Ceram. Soc. 11 (4), 291–298. http://dx.doi.org/10.1016/0955-2219(93)90028-P
42. Dovál, M.; Palou, M.; Kovár, V. (2006) Hydration and microstructure of binder compounds containing C2AS and C2S synthesized by sol-gel method. Ceramics-Silikáty 50 (2), 106–114.
43. Hong, S.H.; Young, J.F. (1999) Hydration kinetics and phase stability of dicalcium silicate synthesized by the Pechini process. J. Am. Ceram. Soc. 82 (7), 1681–1686.
44. Zeng, L.; Li, Z. (2014) Solubility of dicalcium silicate in the NaOH–NaAl(OH)4–Na2CO3 solutions: Determination and prediction. Hydrometallurgy 147, 127–133. http://dx.doi.org/10.1016/j.hydromet.2014.05.007



Copyright (c) 2017 Consejo Superior de Investigaciones Científicas (CSIC)

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.


Contact us materconstrucc@ietcc.csic.es

Technical support soporte.tecnico.revistas@csic.es