Complementary testing techniques applied to obtain the freeze-thaw resistance of concrete

Authors

  • H. L. Romero Universidad Politécnica de Madrid
  • A. Enfedaque Universidad Politécnica de Madrid
  • J. C. Gálvez Universidad Politécnica de Madrid
  • M. J. Casati Universidad Politécnica de Madrid

DOI:

https://doi.org/10.3989/mc.2015.01514

Keywords:

Concrete, Freezing-thawing, MIP, Strain measurements

Abstract


Most of the standards that evaluate the resistance of concrete against freeze-thaw cycles (FTC) are based on the loss of weight due to scaling. Such procedures are useful but do not provide information about the microstructural deterioration of the concrete. The test procedure needs to be stopped after several FTCs for weighing the loss of material by scaling. This paper proposes the use of mercury-intrusion-porosimetry and thermogravimetric analysis for assessing the microstructural damage of concrete during FTCs. Continuous strain measurement can be performed without stopping the FTCs. The combination of the above techniques with the freeze-thaw resistance standards provides better and more precise information about concrete damage. The proposed procedure is applied to an ordinary concrete, a concrete with silica fume addition and one with an air-entraining agent. The test results showed that the three techniques used are suitable and useful to be employed as complementary to the standards.

Downloads

Download data is not yet available.

References

1. Ho, E.; Gough, W.A. (2006) Freeze thaw in Toronto, Canada in a changing climate. Theoretical and Applied Climatology, 83, 203–210. http://dx.doi.org/10.1007/s00704-005-0167-7

2. Mays, G. (2003) Durability of Concrete Structures, Investigation, Repair and Protection, Taylor & Francis, London.

3. UNE-CEN/TS 12390-9 EX (2008). Freeze-thaw resistance, surface mass loss.

4. Valenza, II, J.J.; Scherer, G.W. (2007) A review of salt scaling: I. Phenomenology. Cem. Concr Res. 37, 1007–1021. http://dx.doi.org/10.1016/j.cemconres.2007.03.005

5. Sahin, R.; Tasdemir, M.A.; Gu.l, R.; Celik, C. (2007) Optimization Study and Damage Evaluation in Concrete Mixtures Exposed to Slow Freeze-Thaw Cycles. Journal of Materials in Civil Engineering ASCE, 609–615. http://dx.doi.org/10.1061/(ASCE)0899-1561(2007)19:7(609)

6. Mao, J.; Ayuta, K. (2008), Freeze-Thaw Resistance of Lightweight Concrete and Aggregate at Different Freezing Rates. Journal of Materials in Civil Engineering ASCE, 20, 78–84. http://dx.doi.org/10.1061/(ASCE)0899-1561(2008)20:1(78)

7. Dombrowski, K.I.; Erfurt, W.; Janssen, D. (2002) Identifying D-cracking susceptible aggregates-a comparison of testing procedures. Proceedings Frost damage in Concrete, RILEM, 221–232.

8. Van Mier, J.G.M.; Van Vliet, M.R.A. (2003) Influence of microstructure of concrete on size/scale effects in tensile fracture. Engineering Fracture Mechanics, 70 [16], 2281–2306. http://dx.doi.org/10.1016/S0013-7944(02)00222-9

9. Uchikawa, H.; Hanehara, S.; Hirao, H. (1996) Influence of microstructure on the physical properties of concrete prepared by substituting mineral powder for part of fine aggregate. Cem. Concr. Res. 26 [1], 101–111. http://dx.doi.org/10.1016/0008-8846(95)00193-X

10. RILEM TC 117 FDC (1995) Draft Recommendation for Test method for the freeze- Thaw Resistance of Concrete- Test with water (CF) of with sodium chloride solution (CDF). Materials and Structures 28, 175–182. http://dx.doi.org/10.1007/BF02473223

11. RILEM TC 176-IDC (2004) Test methods of frost resistance of concrete: CIF-Test: Capillary suction, internal damage and freeze thaw test Reference method and alternative methods A and B. Materials and Structures, 37, 743–753. http://dx.doi.org/10.1617/14143

12. Lomboy, G.; Wang, K. (2009) Effects of Strength, Permeability, and Air void Parameters on Freezing-Thawing Resistance of Concrete with and without Air Entrainment. Journal of ASTM International, 6 [10].

13. Sabir, B.B.; Kouyiali, K. (1991) Freeze-Thaw Durability of Air Entrained CSF Concrete. Cem. Concr. Comp. 13, 203–208. http://dx.doi.org/10.1016/0958-9465(91)90021-9

14. Toutanji, H.; Delatte, N.; Aggoun, S.; Duval, R.; Danson, A. (2004) Effect of supplementary cementitious materials on the compressive strength and durability of short-term cured concrete. Cem. Concr. Res. 34, 311–319. http://dx.doi.org/10.1016/j.cemconres.2003.08.017

15. Appa Rao, G. (2001) Influence of silica fume on long-term strength of mortars containing different aggregate fractions. Cem. Concr. Res. 31, 7–12. http://dx.doi.org/10.1016/S0008-8846(00)00346-X

16. Yacizi, H. (2008) The effect of silica fume and high-volume Class C fly ash on mechanical properties, chloride penetration and freeze- thaw resistance of self-compacting concrete. Constr. Build. Mater. 22, 456–462. http://dx.doi.org/10.1016/j.conbuildmat.2007.01.002

17. Jacobsen, S.; Soether, D.H.; Sellevold, E.J. (1997) Frost testing of high strength concrete: frost/salt scaling at different cooling rates. Materials and Structures, 30, 33–42. http://dx.doi.org/10.1007/BF02498738

18. Persson, B. (2003) Internal frost resistance and salt frost scaling of self-compacting concrete. Cem. Concr. Res. 33, 373–379. http://dx.doi.org/10.1016/S0008-8846(02)00968-7

19. Kreisel, R.C.; French, C.E.; Snyder, M.B. (1998) Freeze-Thaw Durability of high-Strength Concrete. Technical final report, Dept. of Civil Engineering, University of Minnesota.

20. Al-Assadi, G.; Casati, M.J.; Fernández, J.; Gálvez, J.C. (2011) Effect of the curing conditions of concrete on the behaviour under freeze-thaw cycles. Fatigue and Fracture of Engineering Materials and Structures, 34 [7], 461–469. http://dx.doi.org/10.1111/j.1460-2695.2010.01520.x

21. ASTM C 143-00 (2000) Standard test method for slump of hydraulic cement concrete.

22. ASTM C231-04 (2004) Standard test method for Air Content of freshly mixed concrete by the pressure method.

23. ASTM C39-01 (2001) Standard test method for compressive strength of cylindrical concrete specimens.

24. UNE-EN 1239-08 (2001) Testing hardened concrete - Part 8: depth of penetration of water under pressure.

25. ASTM C496-90 (1990) Standard test method for splitting tensile strength of cylindrical concrete specimens.

26. ASTM C469-87a. (1987) Standard test method for static modulus of elasticity and poisson's ratio of concrete in compression.

27. Romero, H.L. (2011) Deterioro del hormigón sometido a ensayos acelerados de hielo-deshielo en presencia de cloruros. Ph.D. Thesis. Universidad Politécnica Madrid.

28. ASTM D4404-84 (2004) Standard test method for determination of pore volume and pore volume distribution of soil and rock by mercury intrusion porosimetry.

29. Pane, I.; Hansen, W. (2005) Investigation of blended cement hydration by isothermal calorimetry and thermal analysis. Cem. Concr. Res. 35, 1155–1164. http://dx.doi.org/10.1016/j.cemconres.2004.10.027

30. Sabir, B.B. (1997) Mechanical Properties and Frost Resistance of Silica fume Concrete. Cem. Concr. Comp. 19, 285–294. http://dx.doi.org/10.1016/S0958-9465(97)00020-6

31. Mirza, F.A.M.; Al-Mukarramah, M. (2009) Effect of Sand Replacement and Silica Fume Addition on Chloride Ion Permeability of Lightweight Concrete. JKAU: Engineering Science, 61–73. http://dx.doi.org/10.4197/eng.20-1.4

32. Kearsley, E.P.; Wainwright, P.J. (2001) Porosity and permeability of foamed concrete. Cem. Concr. Res. 31, 805–812. http://dx.doi.org/10.1016/S0008-8846(01)00490-2

33. Neville, A.M. (1999) Properties of Concrete, Fourth and Final Edition, Pearson education limited, England, 433–528.

34. Powers, T.C. (1968) The Properties of Fresh Concrete, John Wiley and Sons, Inc.; New York, 1968.

35. Detwiler, R.J.; Mehta, P.K. (1989) Chemical and physical effects of silica fume on the mechanical behavior of concrete. ACI Mater. J. 86 [6], 609–614.

36. Scrivener, K.L.; Crumbie, A.K.; Laugesen, P. (2004) The interfacial transition zone (ITZ) between cement paste and aggregate in concrete. Interface. Science, 12, 411–421. http://dx.doi.org/10.1023/B:INTS.0000042339.92990.4c

37. Bishnoi, S.; Uomoto, T. (2008) Strain–temperature hysteresis in concrete under cyclic freeze–thaw conditions. Cem. Concr. Comp., 30, 374–380. http://dx.doi.org/10.1016/j.cemconcomp.2008.01.005

38. Jacobsen, S.; Lindgård, J.; Fritz, L. (2008) In: Frost dilation measurements on concrete cores from a dam with ASR. 13th ICAAR conference proceedings; Trondheim. 131–142.

39. Penttala, V.; Al-Neshawy, F. (2002) Stress and strain state of concrete during freezing and thawing cycles. Cem. Concr. Res. 32 [9], 1407–1420. http://dx.doi.org/10.1016/S0008-8846(02)00785-8

40. Hasan, M.; Sato, Y.; Ueda, T. (2008) Stress-strain relationship of frost-damaged concrete subjected to fatigue loading. Journal of Materials in Civil Engineering, 20–37. http://dx.doi.org/10.1061/(asce)0899-1561(2008)20:1(37)

41. Aligizaki, K.K. (2006) Pore Structure of Cement-Based Materials, Testing, Interpretation and Requirements, Abingdon, Oxford, Taylor & Francis.

42. Klemm, A.J.; Klemm, P. (1997) The effects of the alternate freezing and thawing cycles on the pore structure of cementitious composites modified by MHEC and PVA. Build. Environ. 23 [6], 509–512. http://dx.doi.org/10.1016/S0360-1323(97)00025-5

43. Lea, F.M. (1974) The chemistry of cement and concrete. 4th ed. Edward Arnold.

44. Ubbraco, P.; Calabrese, D. (1998) Solidification and stabilization of cement paste containing fly ash from municipal waste. Thermochimica acta, 321 [1, 2], 143. http://dx.doi.org/10.1016/s0040-6031(98)00453-5

Published

2015-03-30

How to Cite

Romero, H. L., Enfedaque, A., Gálvez, J. C., & Casati, M. J. (2015). Complementary testing techniques applied to obtain the freeze-thaw resistance of concrete. Materiales De Construcción, 65(317), e048. https://doi.org/10.3989/mc.2015.01514

Issue

Section

Research Articles

Most read articles by the same author(s)