This paper compares different experimental methods for measuring water permeability in 17 different porous building rocks. Both commercial apparatus and specially made designed permeameters are used for characterising intrinsic permeability and hydraulic conductivity, k, of rocks in the range of 10−12 to 10−4 m/s (∼ 10−19–10−11 m2 or ∼ 10−4–104 mD). We use both falling head and constant head permeameter methods including the triaxial and modified triaxial tests and a classical constant head permeameter.
Results showed that for very low and low permeability samples (k<10−6 m/s), triaxial conditions were found the most accurate procedures and they provided similar or slightly lower permeability values than constant and falling head methods. The latter techniques were highly recommended for permeable and high permeable porous building materials. Water permeability values were also linked to effective porosity and interpreted in terms of interparticle and vugs porosity. Finally, some modifications in the apparatus and procedures were carried out in order to assess water permeability in soft materials, which involve the use of non-saturated samples.
Se caracterizó la permeabilidad intrínseca y conductividad hidráulica, k, con valores que varían desde 10−12 a 10−4 m/s (∼ 10−19–10−11 m2 or ∼10−4–104 mD). Para muestras poco y muy poco permeables el ensayo con célula triaxial fue el mas reproducible. Los ensayos de carga constante son muy recomendables para rocas porosas de construcción permeables y muy permeables. Además, se definen los parámetros experimentales más apropiados para caracterizar la permeabilidad de rocas de construcción. La permeabilidad al agua se relaciona con la porosidad efectiva y se interpreta en términos de porosidad tipo interpartícula y vugs. Finalmente, se modificaron los equipos y procedimientos para poder estimar la permeabilidad en materiales blandos.
Permeability measures the material's ability to transmit fluids and can be termed in different ways depending on the field. Permeability, coefficient of permeability or intrinsic permeability depends only on the pore structure of the material, it is independent of fluid properties and it is based in the Darcy's equation. Permeability has units with dimensions of area (m2). A practical unit for permeability is the darcy (D), or more commonly the millidarcy (mD) (1D ∼10−12m2). Hydraulic conductivity is usually referred to permeability or coefficient of permeability and it is related to intrinsic permeability (pore structure) and to the properties of the fluid (dynamic viscosity of the fluid and specific gravity of the fluid). Hydraulic conductivity has units with dimensions of length per time or speed (e.g., m/s, cm/day or ft/day). Thus, for pure water at 20 °C, 1D ∼10−12m2 ∼10−5 m/s. In this paper, we use the term water permeability for both intrinsic permeability and hydraulic conductivity, so that, a special attention to permeability units should be given in order to understand what parameter is mentioned.
Saturated water permeability of construction and building materials, including stone, concrete and bricks, is seldom the dominant transport mechanism in real situations. Real mass transfer takes place by two-phase flow in which the vapour component is dominant. Nevertheless, there are particular cases where water permeability is the predominant transport mechanism. For instance, stagnant water due to rains may affect ancient and modern buildings and monuments such as fountains, terraces and basements (
Saturated permeability has been of great interest since it quantifies the connectivity of the pore structure and assesses the durability of construction and building material. The influence of pore structure and water transfer on durability can greatly vary depending on the nature of the building rock. Thus, porous materials with low porosity values (<10%) have low water transfer coefficients, and are also more durable than highly porous rocks. For example, dense oolitic and microcrystalline limestones, granites or marbles present low porosity and permeability, and have excellent durability properties (
Furthermore, air surface permeability has been used to estimate salt deterioration in both lab and monuments studies (
Most common existing standard tests to measure water permeability can be divided into two different groups, depending on the head loss or inflow pressure variation/constancy. Constant head methods maintain constant the hydraulic pressure or head whereas inflow pressure decreases due to variation of water column in falling head methods.
There is a lack of water permeability standard tests of building stones. Most standard tests of rock permeability use flowing air instead of water (for instance, ASTM D4525-90 (
The aim of this paper is to compare different experimental methods for measuring water permeability of porous building rocks. Laboratory methods are based and adapted from standard tests used in cementitious materials and soil sciences. For this purpose, both commercial apparatus and specially made designed permeameters are used for characterizing stone permeability in the range of ∼10−12–10−4 m/s; ∼10−19–10−11 m2; or ∼10−4–104 mD.
Finally, some modifications of the apparatus and procedures are carried out in order to assess water permeability in soft materials, such as soft rocks, ancient and repair mortars, etc. The interest of measuring water permeability in this kind of porous rocks is increasing in the field of built heritage, where stones may be weathered; CO2 storage, etc. Soft materials may be altered in contact with water, compromising sample preparation and permeability testing. Thus, if sample loses material, it can damage the permeameter and/or produce inaccurate measurements. Researches tend to characterise the permeability using gas permeameters, which are usually more expensive. Nevertheless, real water flow value is sometimes required.
In this study, 17 samples of porous stones have been chosen for their different petrophysical and petrographic characteristics (
Image of the studied samples. C: biocalcarenites. T: travertines. L: allochem limestones. S: silica cement sandstones.
The studied biocalcarenites are carbonate sandstones with calcite cement, variable amount of terrigenous components and fossils (mainly foraminifera) and interparticle porosity. C1 is a variety of the Piedra de Úbeda (
The studied travertines are quarried in Albox (Almería province, SE of Spain) and are commercialised as Travertino Oro or Yellow Gold Travertine. Currently, this yellowish-brown travertine is mainly used as cladding and paving. The studied travertines present different structural (mesofeatures) and textural (microfeatures) characteristics (
Allochem limestones show a wide range in the size and type of allochems. These limestones mainly have interparticle porosity. L10 and L11 are detrital limestones (biorrudites) composed of large allochem grains (mainly bivalves, bryozoans and red algae) (
Quartz-rich sandstones are well-sorted sandstones and cemented by secondary (authigenic) quartz. S16 is mainly composed of monocrystalline quartz grains (
Effective porosity, Ø
Dried samples were weighed and placed in a vacuum chamber at 20±7 mbar pressure controlled by a vacuum manometer. Three 24-hour cycles were carried out for each. Firstly, any trapped air was eliminated from the porous systems. Secondly, distilled water was slowly introduced until the samples were completely covered. Thirdly, atmospheric pressure was re-established in order to avoid porous system dilatation. Then the saturated and immersed weight of each sample was recorded.
Permeability measurements were performed in the same cylindrical samples as those performed in the effective porosity test. Permeability was measured on water saturated samples. Thus, after effective porosity characterisation, vacuum saturated samples were then tested. Finally, some non-saturated samples were saturated during the inflow of water and permeability was calculated when steady-state was reached (water flow rate at inflow equals to water outflow rate). In this paper, we use three constant head methods (triaxial test, modified triaxial test and classical constant head permeameter) and two failing head methods. Four measurements were performed in each sample. The maximum duration of each experiment was 24 hours in order to assess what method was more adequate for relatively fast permeability characterisations.
Permeability tests were carried out in a triaxial device (
Triaxial method. Schematic diagram of triaxial cell. (A). Triaxial method apparatus. (B). Pressure maintainers. P1: Confining pressure. P2: Inflow pressure. P3: Outflow pressure. In the TM, outflow pressure is fixed in the end caps and outflow water circulates from equipment. MTM procedure uses the atmospheric pressure as outflow pressure. (C). Triaxial Cell: 1. Movable top-end plate. 2. Rubber joint. 3. Inflow-Outflow pressure entrance. 4. Steel body. 5. Open/close valve. 6. Confining pressure entrance. 7. Nitrile rubber sleeve. 8. Sample. (D). Triaxial cell pieces.
In the triaxial method, water flows through a confined sample from driven, entrance or inflow pressure, P1, to exit or outflow pressure, P0. Two variations of the triaxial method were preformed modifying the outflow pressure, which were termed as TM (triaxial method) and MTM (modified triaxial method). In the TM, outflow pressure is fixed in the end caps and outflow water circulates from equipment. MTM procedure uses the atmospheric pressure as outflow pressure, so that water does not remain in the permeameter. The latter can be adequate for testing soft material, in which loss material can be probable.
The confining, inflow and outflow pressures in the TM were respectively of 13 bar, 7 and 3 bars. These experimental conditions were used for all the tested samples. However, in the MTM, the inflow pressure was adjustable to each porous stone in order to reach reproducible results. The confining pressure was 13 bars whereas the outflow pressure was the atmospheric pressure.
In general, low permeable rocks request higher inflow pressure. Thus, an inflow pressure of 10 bar was used for testing C1, L12, L13 and L17 samples; P1=7 bars for testing C2, C3, C4, C5, C6 and L16 samples; and P1=5 bars for T7, T8, T9 and L14 samples. The confining pressure (1.3 MPa) was lower than the unconfined compressive strength, which ranges between 10–70 MPa for the studied samples (
Samples were placed in a nitrile rubber sleeve, to which the confining pressure is applied. Thus, samples were not laterally sealed with PTFE and/or with a shrinkable sleeve, as they were performed at constant and falling head permeability methods.
Water permeability (intrinsic permeability), k (m2), was determined according to Darcy's Equation [
where η is the water viscosity kg/(ms), Q (m3/s) is the volumetric flow-rate of water, L (m) is the length of the sample, A (m2) is the cross-sectional area of the sample perpendicular to the direction of flow and ΔP =P1−P0 (Pa) is the pressure gradient.
A laminar (steady-state) flow rate with a constant pressure is achieved when the X-Y plot is a straight line. This equipment provides very accurate permeability measurements from values ∼10−11–10−5 m/s or ∼10−18–10−12 m2.
The apparatus (
Constant head permeameter: (A). Constant head apparatus. (B). Schematic diagram: 1. Tank with over flow. 2. Inflow water. 3. Outflow water. 4. Water exit to the sample. 5. Valve to fit the sample. 6. Valve to purge the sample. 7. Sample. (C). Sample preparation: 1. PVC connection cup. 2. PVC screw fitting. 3. Heat shrinkable sleeve. 4. Adjusting flange. 5. PTFE. 6. Sample.
The sample was sealed, as described in the falling head method, covering its lateral surface with a single length of PTFE first. Over the sample, it was placed a heat shrinkable sleeve that is shrank with hot air to minimize its diameter. The neck of the prepared sample was narrower than the body so the sample fitted the PVC cap perfectly.
The water permeability or hydraulic conductivity, k (m/s), of the sample is determined from Eq. [
where
In the present study, two variations of falling head methods have been tested. The first method comprised a panel of 8 tubes (
Falling head permeameter (8 tubes). (A). Falling head apparatus (8 tubes). (B). Schematic diagram: 1. Crystal tube. 2. Valve to fit the sample. 3. Valve to purge the sample. 4. Sample. (C). Sample preparation: 1. PVC connection cup. 2. PVC screw fitting. 3. Heat shrinkable sleeve. 4. Adjusting flange. 5. PTFE. 6. Sample.
Falling head permeameter (Single graduated cylinder). (A). Falling head apparatus. (B). Schematic diagram: 1. Graduated cylinder. 2. PVC screw fitting. 3. PVC cell to house the sample. 4. Rubber joint. 5. PTFE. 6. Sample. 7. End piece to fit the PVC cell into the container. 8. Container to collect the water.
The multiple tubes permeameter had 8 crystal tubes of 100 cm height and 9 mm diameter attached for wall mounting. The standpipe was connected by a two arm valve (as described for the constant head permeameter): one of the arms was used to purge the air before beginning the test and the other was used to fit the sample using a rubber cap that fitted the sample perfectly. Each tube had its own standpipe connector in order to control the flow individually. On the floor, beneath the permeameter, there was a container to collect the water that had passed through the sample. It is possible to test 8 samples at the same time but it is strongly recommended that the testing of each sample is separated by 2 minutes from the beginning of the previous test. To start the test, the tube was filled with water and air was removed from the column by the standpipe. Once the air had been removed and the water level remained stable the height of water corresponded to time 0 and the experiment could start. The different heights of water are recorded per unit time.
The second method (single graduated cylinder) had a specially made design and consisted of a graduated cylinder thread connected to a PVC cell. This method aims to show a cost-effective solution suited to investigating rock with medium-high permeability values. The method is easy to perform and adapt to different sample dimensions, and also it is inexpensive, versatile and portable. The used graduated cylinder was in the form of 27 mm diameter and 235 mm height. The base of the graduated cylinder was removed and adapted in order to thread it to the PVC cell via a screw fitting. Several rubber joints were used to adapt the height sample to the PVC cell. Both, PVC cell and the screw are typical DIY pieces. In the bottom there was a fitting container to collect the water that flew through the pores of the sample. To obtain water permeability, the tube was filled by water and different heights of water were recorded per unit time.
In both methods, samples were laterally sealed with PTFE and a heat shrinkable sleeve using the same methodology performed in the constant head method.
Water permeability or hydraulic conductivity, k (m/s), of the sample is calculated using the following equation [
where
Effective porosity, Ovs, and water permeability obtained using different methods: triaxial (TM), modified triaxial (MTM), constant head and falling head. (-) Non-reproducible values using the experimental conditions of this study. Samples are classified (Hölting classification) into 3 groups considering results from de TM
Sample | Effective porosity, p (%) | Water permeability or hydraulic conductivity, k (m/s) | Water permeability or intrinsic permeability, k (m2) | Hölting Permeability Classification | ||||||
---|---|---|---|---|---|---|---|---|---|---|
|
||||||||||
TM | MTM | Constant Head | Falling Head | TM | MTM | Constant Head | Falling Head | |||
C1 | 3.87 | 2.10E-11 | 5.20E-10 | – | 6.20E-10 | 2.10E-18 | 5.20E-17 | – | 6.20E-17 | |
T7 | 7.04 | 1.00E-10 | 1.40E-10 | – | 2.30E-09 | 1.00E-17 | 1.40E-17 | – | 2.30E-16 | |
T8 | 12.54 | 1.00E-10 | 6.30E-12 | – | 6.00E-10 | 1.00E-17 | 6.30E-19 | – | 6.00E-17 | |
C4 | 16.70 | 1.06E-10 | 1.20E-09 | – | 3.09E-10 | 1.06E-17 | 1.20E-16 | – | 3.09E-17 | Very low permeable |
L12 | 8.62 | 5.10E-10 | 7.00E-10 | – | 2.10E-09 | 5.10E-17 | 7.00E-17 | – | 2.10E-16 | |
T9 | 8.46 | 9.00E-10 | 6.00E-10 | – | 1.00E-09 | 9.00E-17 | 6.00E-17 | – | 1.00E-16 | |
C2 | 20.61 | 2.26E-09 | 1.60E-09 | – | 6.90E-09 | 2.26E-16 | 1.60E-16 | – | 6.90E-16 | |
C6 | 26.71 | 8.39E-09 | 2.47E-08 | – | 5.10E-09 | 8.39E-16 | 2.47E-15 | – | 5.10E-16 | |
L14 | 11.99 | 1.09E-08 | 1.77E-08 | – | 1.09E-08 | 1.09E-15 | 1.77E-15 | – | 1.09E-15 | |
S16 | 13.10 | 2.02E-08 | 3.30E-08 | – | 2.70E-09 | 2.02E-15 | 3.30E-15 | – | 2.70E-16 | |
C3 | 22.02 | 6.27E-08 | 5.33E-08 | 1.06E-08 | 1.41E-08 | 6.27E-15 | 5.33E-15 | 1.06E-15 | 1.41E-15 | |
L13 | 22.05 | 8.32E-08 | 5.38E-08 | 8.70E-09 | 2.47E-08 | 8.32E-15 | 5.38E-15 | 8.70E-16 | 2.47E-15 | Low permeable |
S17 | 16.05 | 1.05E-07 | 3.60E-08 | 9.90E-09 | 1.45E-08 | 1.05E-14 | 3.60E-15 | 9.90E-16 | 1.45E-15 | |
C5 | 23.56 | 1.06E-07 | 2.55E-08 | – | 4.50E-09 | 1.06E-14 | 2.55E-15 | - | 4.50E-16 | |
L15 | 18.87 | 2.28E-06 | – | 1.35E-07 | 8.80E-07 | 2.28E-13 | – | 1.35E-14 | 8.80E-14 | |
L10 | 20.35 | 2.93E-06 | – | 2.75E-06 | 7.72E-06 | 2.93E-13 | – | 2.75E-13 | 7.72E-13 | Permeable |
L11 | 19.01 | 1.25E-05 | – | 6.36E-06 | 1.09E-05 | 1.25E-12 | – | 6.36E-13 | 1.09E-12 |
Considering results from the TM, eight varieties of the studied building stones (C1, C2, C4, C6, T7, T8, T9, L12) are classified as very low permeability rocks, other six (C3, C5, L12, L14, S16, S17) are low permeable and the last three (L10, L11, L15) are permeable.
For very low permeable samples, in general, water permeability values obtained with TM present similar or slightly higher values than those MTM and similar or slightly lower than falling head method. However, we did not acquire reproducible values using the constant head method for 24 hours of testing. This could be improved by increasing the height of the water column and/or the test duration.
Hydraulic conductivity abacuses for the falling head method. Experimental parameters: height and diameter, dcol, of the water column, testing time and size (diameter, d, and length, L) of the sample for the height variation from initial head, h0, to final head, h.
For low permeability samples (10−6<k<10−8 m/s), in general, water permeability values obtained with TM and MTM methods present similar values and they are slightly higher values than those obtained from constant and falling head methods. Most samples can be tested using all the studied methods. Samples C5, L13 and S17 showed the most dispersed results between the different tested methods.
The permeable building rocks (L9, L10 and L15) showed comparable values in the tested permeability methods. For this kind of permeable materials, MTM method cannot be used, and therefore recommended, since equipment cannot reach the inflow pressure due to the fast water flow through the porous rock. This problem is also found for the TM in high permeable materials, so that, both constant and falling head methods are highly recommended for permeable and high permeable porous building materials.
The two variations of falling head methods studied in this paper provide, in general, comparable values. However, the measurement of the water height variation in the graduated cylinder is not as satisfactory as in the falling head-8 tubes method, and therefore, does not provide accurate results. For that reason,
Ranges of water permeability for each tested method.
Test method | Hydraulic conductivity (m/s) | Intrinsic permeability (m2) |
---|---|---|
Triaxial | 10−11<k<10−5 | 10−18<k<10−12 |
Modified triaxial method | 10−9<k<10−7 | 10−16<k<10−4 |
Constant head permeameter | k>5.10−8 | k>5.10−15 |
Falling head permeameter | 10−10<k<10−6 | 1−17<k<10−13 |
The classical permeability – porosity relationship based in Lucia's classification is showed in
Permeability – porosity relationship based in the Lucia's classification of the studied porous building rocks. Horizontal divisions correspond to Hölting classification.
Encouraging results were obtained using non-saturated samples. The MTM was used for several very low permeable and low permeable samples whereas the falling head method was applied to several low permeable and permeable samples. Water permeability values obtained using MTM method of the samples C2, C3, C4, C5 and Q7 were, respectively, 1.57·10−9, 5.52·10−8, 7.10·10−10, 9.43·10−8 and 1.73·10−8 m/s; whereas using falling head method characterisation of the samples C3, Q7, L9 and L10 were 3.49·10−8, 3.70·10−8, 4.68·10−4, and 3.74·10−5 m/s. Consequently, for low permeable and permeable samples, satisfactory water permeability values can be obtained in non-saturated samples when steady-state is reached. Moreover, from the practical point of view, the permeameter cell of the falling head method can test samples with different sizes and forms, such as prismatic forms (
In this paper, different laboratory methods have been employed and adapted from standard tests used in cementitious materials and soil sciences field. Seventeen porous rocks have been chosen for their different petrophysical and petrographic characteristics, which are used as building materials or found in the Spanish built heritage. The characterisation of rock permeability and hydraulic conductivity, k, was carried out in the range of 10−12 to 10−4 m/s (∼10−19–10−11 m2 or ∼10−4–104 mD).
The maximum duration of each experiment was 24 hours in order to assess what method was more adequate for relatively fast permeability characterisations. In order to achieve the most appropriated combination of experimental parameters for a given rock permeability, different abacuses were plotted, in which height and diameter of the water column, testing time and sample size can be changed.
A modified Lucia's plot defined permeability fields of rocks with visible interparticle pores at hand specimen. Rock specimens with large interparticle pores (pores visible at first glance) and high values of effective porosity present high water permeability values. In particular, travertine T8 shows separated vugs that contribute to porosity but not to water permeability whereas T9 has both separated and touching vugs, and therefore shows a water permeability value higher than the other travertines.
Finally, some modifications of the apparatus and procedures were carried out using non-saturated samples in order to assess water permeability in soft materials, such as soft rocks, ancient and repair mortars. The modified triaxial method was found to be the most appropiated procedure for several very low permeable and low permeable samples, whereas falling head method for several low permeable and permeable samples.
This study was financed by the Spanish Ministry of Science and Innovation CGL2011-25162. A pre-doctoral research fellowship was awarded to C. Pla for this project.