The ageing of asphalt mixes, together with their exposure to low temperatures, causes a progressive increase of cracking. In this paper, the effect of ageing and temperature on the fatigue of asphalt concretes made with two types of binders, conventional (50/70) and polymer modified bitumen (PMB), is studied. For this purpose, specimens previously subjected to an accelerated laboratory ageing process were tested by a strain sweep test at different temperatures (-5ºC, 5ºC and 20°C). Results were compared with the obtained from the unaged specimens showing the relative importance of ageing, temperature and type of bitumen on the parameters that determine the fatigue life of the mixture. The mixtures behaviour becomes more brittle with ageing and the decrease of temperature. However, ageing hardly has an effect on fatigue at lower temperatures. In general, mixtures made with polymer modified bitumen have a better fatigue performance to ageing and temperature.
Asphalt layers suffer a progressive deterioration when they are exposed to repeated loads caused by traffic and environmental conditions such as heat, wind, rain or ultraviolet radiation. All of these factors lead to an increase of cracking of the asphalt layers in the pavement structure, which leads to them breaking up (
An important factor in cracking resistance of mixtures due to fatigue is ageing (
Ageing occurs in two stages (
There are a number of methods for artificially ageing bituminous mixtures in the laboratory. The basic procedure involves exposing the mixture to high temperatures for a specified period of time. Much of the research on ageing in asphalt mixtures follows the ageing procedure established by the SHRP (
A bituminous mixture should be designed and manufactured not only to withstand the traffic loads imposed, but also the action of the environment (
The fatigue behaviour of bituminous mixtures has been studied extensively in the last four decades. Because of the fact that it is a complex phenomenon and is influenced by many factors, there is not now a universal testing procedure to characterize it completely. The classical fatigue tests, described in the current standards (EN and ASTM), are time sweep tests. They are usually based on the application of a cyclic load under controlled conditions of strain or stress until failure of the mixture occurs.
In order to estimate the fatigue law, several samples are tested under different amplitudes of stress/strain (
The paper presented here studies the effect of ageing on the fatigue behaviour of an asphalt mixture. This mixture, a bituminous concrete type, is made with two types of bitumen, a penetration bitumen and a polymer modified bitumen. The fatigue behaviour will be analyzed at different temperatures by applying a strain sweep test, called EBADE (the initials of the strain sweep test in Spanish, Ensayo de Barrido de Deformaciones) (
A semi-dense bituminous mixture was selected to study the effect of ageing on the fatigue behaviour of bituminous mixtures. This type of mixture was an asphalt concrete (AC16S, according to the Spanish Specifications) and the particle size was centred on the envelope (
Bitumen characteristics
Properties | Unit | Standard | 50/70 | PMB 45/80-65 |
---|---|---|---|---|
Penetration at 25ºC | (0.1 mm) | EN 1426 | 61 | 57 |
Softening Point R&B | (ºC) | EN 1427 | 50.9 | 65.3 |
Fraass breaking point | (ºC) | EN 12593 | -14 | -15 |
Flash Point | (ºC) | EN 2592 | 280 | 290 |
Mass variation | (%) | EN 12607-1 | 0.1 | 0.29 |
Penetration at 25ºC | (% p.o.) | EN 1426 | 66 | 64 |
∆ Softening Point | (ºC) | EN 1427 | 7.6 | 10 |
Summary of the experimental study carried out
Mixture | Bitumen | Conditioning | Test temperature (ºC) |
---|---|---|---|
AC16S | 50/70 | Unconditioned | −5 |
5 | |||
20 | |||
Aged | −5 | ||
5 | |||
20 | |||
PMB 45/80-65 | Unconditioned | −5 | |
5 | |||
20 | |||
Aged | −5 | ||
5 | |||
20 |
Grain size distribution for the mixture AC16S.
Long-term ageing of the mixture was simulated in the laboratory by maintaining the loose mixture at 85ºC for 7 days. During the ageing, the mixture was stirred three times, on days 2, 4 and 5, with a time interval between agitations greater than 24 hours. Although the RILEM recommendations establish 9 days, De La Roche,
Unaged and aged specimens were tested by EBADE test to evaluate the fatigue behaviour of the mixture and analyze the effect of ageing. This test consists of performing a sweep strain in a cyclic tension-compression test. The test is performed by applying a number of cycles at a constant level of strain, which increases gradually in magnitude until the material failure occurs. The EBADE test can be performed at different temperatures. In this case, the test was performed at -5ºC, 5ºC and 20ºC. These temperatures allowed the effect of medium and low temperatures to be evaluated where the fatigue response of the mixture could be more critical.
In the execution of the test, a prismatic specimen was used. Two slots were made in the central area of the specimen to reduce the area in its middle section and induce its failure. Although dimensions of the specimens are not fixed, they are usually 5-6 cm wide and long, and 6-9 cm high (
(a) Specimen dimensions (cm) and (b) specimen during the EBADE test.
During the test, cyclical series of 5,000 repetitions were applied at different strain amplitudes in ascending order at a frequency of 10 Hz. 5,000 cycles were chosen because they are enough to observe the tendency of the dissipated energy density and also allowed the test to be carried out more quickly than the time sweep tests (
The modulus and dissipated energy density during each cycle of the test were calculated as shown in equations [
where σ
The cumulative dissipated energy density was obtained as the sum of all dissipated energy densities, as shown in equation [
Complex modulus, |E*|, versus cycles for the unconditioned (Uncond) and aged mixtures. Bitumen 50/70.
Complex modulus, |E*|, versus cycles for the unconditioned (Uncond) and aged mixtures. Bitumen PMB 45/80-65.
On analyzing the effect of the temperature, firstly, an increase of the initial modulus of the mixture was observed with the decrease of temperature, as was expected. Secondly, on analyzing the evolution of the modulus with the number of cycles, the behaviour observed was clearly different for the different test temperatures considered in this study. At a temperature of 20°C, the modulus tended to decrease progressively as the number of cycles in the test increased. However, the modulus fell more quickly from a certain number of cycles for a temperature of 5ºC. Until then, the value of the modulus tended to remain constant, being quite close to the initial modulus, and the drastic drop of the modulus showed the brittle behaviour of the mixture at low temperatures. At a temperature of -5ºC, the behaviour was even more brittle. In this case, the modulus remained constant until the specimen broke, going from the initial value to a residual value close to zero in the same step.
If the behaviour of each bitumen is compared, the modified bitumen presented initial modulus values lower than those achieved with conventional bitumen for each temperature studied. In addition, the modified bitumen for each temperature was able to withstand a higher number of cycles to reduce the value of the modulus and, therefore, before breaking.
Finally, the ageing effect was analyzed. It was observed that the initial modulus of the aged mixture increased substantially with regard to the modulus of the unaged mixture, both for the mixture manufactured with conventional bitumen (50/70) and for the mixture made with modified bitumen (PMB 45/80-65). However, for the degree of ageing considered in this work, the increase of the initial modulus due to the ageing of the mixture was less than that produced due to the test temperature decrease. At low temperatures (-5°C), ageing hardly affected the complex modulus especially in the case of the mixture made with conventional bitumen. At that temperature, the mixture had such a rigid behaviour that the modulus could no longer increase.
In any case, the mixture increased its modulus as it was stiffened either by ageing or by decreasing the temperature. This produced a decrease in the number of cycles that the mixture could withstand before the modulus decreases.
Dissipated Energy Density versus cycles for the Unconditioned (Uncond) and aged mixtures. Bitumen 50/70.
Dissipated Energy Density versus cycles for the unconditioned (Uncond) and aged mixtures. Bitumen PMB 45/80-65.
The greater the maximum dissipated energy density, the higher the temperature, the curves in the figures tended to move to the right, which means a greater number of cycles to halve the peak of the dissipated energy density. The mixture was capable of withstanding fewer strain steps before the mixture failed when the temperature decreased. This showed a sudden change in the dissipated energy density, this was more pronounced at lower temperatures, similar to the trends observed for the modulus of the mixture.
These figures also show how unaged mixtures, made from either of the bitumens, could accumulate a larger amount of dissipated energy during the fatigue process than the aged mixtures (as was the case with the mixture tested at the highest temperature).
In the case of unaged mixtures, several strain steps were necessary for the mixture failure to occur, once the energy in each cycle started to decrease. Whereas mixtures broke faster (for a lower number of cycles) and more abruptly (less steps) when they were aged, showing a more brittle behaviour (
The response of both bitumens is compared. The mixture made with the modified bitumen (PMB 45/80-65) showed how it not only dissipated more energy than the mixture made with conventional bitumen (50/70), but also several strain steps were necessary for breaking after ageing. However, the mixture made with conventional bitumen broke in a single strain step. This fact was also observed when the temperature decreased, indicating that the modified bitumen has a better performance against ageing and temperature variation. Nevertheless, for a very low temperature test, the behaviour of both bitumens was similar, showing that the type of bitumen has less effect on the behaviour of the mixture.
Initial modulus for the unconditioned (Uncond) and aged mixtures.
According to the failure criterion specified in the EBADE test, the failure strain was defined as the value equivalent to the strain step in which the maximum dissipated energy density was reduced to half. The failure strain values for all the conditions of the study are shown in
Failure strain for the unconditioned (Uncond) and aged mixtures.
Finally, by comparing the response of both bitumens it was shown that the modified bitumen resisted higher strain before breaking, for all the conditions studied. Nevertheless, it was also observed that the modified bitumen mixture was more susceptible to the effects of ageing and temperature than the conventional bitumen one. Similar conclusions were obtained by Miró,
Comparing the values of the initial modulus with the failure strain values, failure strain increased as the initial modulus values decreased. This indicates that the increase in the stiffness of the mixture increases its brittleness, and it can withstand lower strain values.
Cumulated dissipated energy density for the unconditioned (Uncond) and aged mixtures.
On the other hand, cumulative dissipated energy density for the mixture made with conventional bitumen was noticeably lower than the one made with modified bitumen for medium test temperatures. In either case, it decreased as the mixture aged.
Failure strain versus complex modulus, |E*|, for the unconditioned (Uncond) and aged mixtures.
The curves obtained when the temperature of the unaged and aged mixtures decreased for each of the bitumen almost overlapped and tended to converge in one area, regardless of the type of bitumen used. Although the range of values through which they move and how quickly was different for each bitumen. So, the mixture made with modified bitumen started from lower modulus values and higher strain values (at 20°C without ageing) than the mixture made with conventional bitumen. Furthermore, the slope of the modulus-strain curve was greater for the mixture manufactured with modified bitumen than for the one made with conventional bitumen.
The convergence of the curves suggests that, regardless of the type of bitumen used and the conditions to which the mixture was subjected (more or less aged), critical values of modulus and failure strain is reached by lowering the temperature. These values are characteristics of each type of mixture.
In this paper the effect of ageing, test temperature and type of bitumen in the fatigue behaviour of a semi-dense bituminous mixture, a bituminous concrete type, have been studied. A tension-compression strain sweep test, EBADE test, was applied. For this, the mixture was manufactured from two different bitumens (a conventional bitumen, 50/70, and a polymer modified bitumen, PMB 45/80-65). This mixture was aged rapidly in the laboratory by keeping the loose mixture in an oven at 85°C for 7 days. Specimens were tested at different temperatures (-5ºC, 5ºC and 20°C), and their response compared with the same mixture unaged.
The EBADE test allows the progressive deterioration of the mixture to be shown with the number of cycles both from the change in the modulus and from the dissipated energy density during the fatigue process. However, this variation is highly dependent on the three variables analyzed in this study: the test temperature, the degree of ageing and the type of bitumen.
For medium temperatures (20°C), the modulus decreases progressively with the number of cycles. But on lowering the temperature, the modulus values suffer a sharp drop from a certain number of cycles. The more brittle behaviour of the mixture is pointed out. As the temperature decreases, the mixture is able to withstand fewer strain steps (fewer number of cycles) before the mixture fails. A more sudden change in the dissipated energy density is shown, the lower the temperature, the sharper the change.
The ageing of the mixture causes the initial modulus to increase substantially compared to the unaged mixture. However, the effect of ageing (for the degree of ageing considered in this work) is smaller than the temperature effect, since the increase of the initial modulus due to the ageing of the mixture is lower than the effect of the test temperature.
As the mixture ages, failure occurs at a lower number of cycles and more steeply (for fewer load steps) than when the mixture is unaged, due to its high degree of brittleness. But at lower temperatures (-5°C), ageing hardly affects the modulus of the mixture. At these temperatures, the mixture displays such stiffness behaviour that the modulus can no longer increase. So its condition (aged or unaged) hardly influences its fatigue life.
The use of different types of bitumen has a significant effect on the fatigue behaviour of the mixture at medium temperatures. In general, although the mixture made with polymer modified bitumen is more susceptible to the effects of ageing and temperature than the one made of conventional bitumen, it has a better response to ageing and temperature. It was shown to be less brittle with a higher failure strain than the mixture made with conventional bitumen. However, the stiffness of the mixture at low temperatures is so high that its behaviour tends to be similar regardless of the type of bitumen used.
The authors would like to thank the Ministry of Economy and Competitiveness (Spain) for its assistance in the project PROFIS (BIA2012-36508), established within the framework of the VI National Plan for Scientific Research, Development and Technological Innovation (RDI), co-financed with funds from the European Regional Development Fund (ERDF) of the European Union. The work of the first author was partially funded by the Ministry of Economy and Competitiveness, Spain (Research Grant BES-2013-065678). The authors would also like to acknowledge the company CEPSA for supplying and characterizing the bitumen used in this study.