Evaluation of particleboard with Pine wood particles using polyurethane resin and polyethylene terephthalate
DOI:
https://doi.org/10.3989/mc.2026.391224Keywords:
Particleboard, Pinus, Polyethylene terephthalate, Waste, PURAbstract
The use of recycled polyethylene terephthalate (PET) with pine wood shavings was analyzed in the particleboard manufacture using hot-pressing. 160 °C was considered to avoid moisture build-up in the resin structure and polymer degradation and, property losses. 50% Pine with 40% PET and 10% polyurethane resin (PUR) and 50% Pine with 50% PET and 0% PUR were studied traits. Density, thickness swelling, water absorption, modulus of rupture, modulus of elasticity, perpendicular tensile properties and scanning electron microscopy (SEM) were studied. Density was close to 1 g/cm³, classifying both traits as high-density panels according to the standard code. SEM showed that 160 °C provided an effective envelopment of wood shavings. Physical and mechanical panel properties were superior to the minimum values of standard codes in 10% PUR trait, while they were lower with 0% PUR.
Downloads
References
SNIF – Sistema Nacional de Informações Florestais. 2020. Boletim SNIF 2020: dados sobre o setor florestal brasileiro. Brasília: Ministério da Agricultura, Pecuária e Abastecimento, Serviço Florestal Brasileiro.
ABIMCI – Associação Brasileira da Indústria de Madeira Processada Mecanicamente. 2020. Dados estatísticos do setor de madeira processada mecanicamente. Curitiba: ABIMCI.
ABIMOVEL – Associação Brasileira da Indústria de Móveis. 2020. Relatório anual de consumo de madeira no setor moveleiro. Brasília: ABIMOVEL.
Pedzik M, Janiszewska D, Rogozinski T. 2021. Alternative lignocellulosic raw materials in particleboard production: A review. Ind. Crops Prod. 174:114162.
De Araujo V, Vasconcelos J, Lahr F, Christoforo A. 2022. Timber forest products: A way to intensify global bioeconomy from bio-materials. Acta Fac. Xylologiae Zvolen. 64(1):99-111.
Guimarães Júnior JB. 2008. Painéis de madeira de eucalipto: estudo de caso de espécies e procedências. M.Sc. Dissertation. Universidade Federal de Lavras, Lavras.
Araujo CKC, de Campos CI, Camargo SKCA, Camargo BS. 2019. Caracterização mecânica de painéis particulados de média densidade produzidos a partir de resíduos de madeira. Revista Gestão Industrial 15(1):197-211.
Iwakiri S, Trianoski R. 2020. Painéis de madeira reconstituída. 2nd.ed. Curitiba: Fundação de Pesquisas Florestais do Paraná. pp-1.259.
Mendes LM, Mendes RF, Guimararães Júnior JB, Santos RC, César AAS. 2012. Efeito da associação de bagaço de cana, do tipo e do teor de adesivo na produção de painéis aglomerados. Santa Maria: Ciência Florestal.
Bertolini MS. 2011. Emprego de resíduos de Pinus sp tratado com preservantes CCB na produção de chapas de partículas homogêneas utilizando resina poliuretano à base de mamona. M.Sc. dissertation. Universidade de São Paulo, São Carlos.
ABIPET – Associação Brasileira da Indústria do PET. 2018. Panorama da indústria do PET no Brasil. São Paulo: ABIPET.
ABIPET – Associação Brasileira da Indústria do PET. 2022. Censo da reciclagem do PET no Brasil: relatório de 2022. São Paulo: ABIPET
ABNT – Associação Brasileira de Normas Técnicas. 2013. NBR 14810-3: Adesivos para madeira - Determinação do teor de sólidos e viscosidade do adesivo poliuretânico. Rio de Janeiro: ABNT.
ABNT – Associação Brasileira de Normas Técnicas. 2013. NBR 14810-1: Chapas de madeira aglomerada - Parte 1: Terminologia. Rio de Janeiro, 2013.
ABNT – Associação Brasileira de Normas Técnicas. 2018. NBR 14810-2: Chapas de madeira aglomerada - Parte 2: Requisitos. Rio de Janeiro, 2018.
ASTM – American Society for Testing and Materials. 2016. ASTM D905-08: Standard test method for strength properties of adhesive bonds in shear by compression loading. West Conshohocken: ASTM International.
Iwakiri S. 2005. Painéis de madeira reconstituída. Curitiba: Fundação de Pesquisas Florestais do Paraná.
Trianoski R. 2020. Adesivos para painéis de madeira: desenvolvimento e aplicações. Curitiba: Editora Técnica Florestal.
Maloney TM. 1993. Modern Particleboard & dry-process fiberboard manufacturing. San Francisco: Miller Freeman Publications.
Coutinho FMB, Delpech MC. 1999. Poliuretanos como materiais de revestimento de superfície. Polímeros 9:41-48.
Mölleken RE. 2017. Aplicação do adesivo poliuretano derivado do óleo de mamona na obtenção de painéis de madeira colados lateralmente. 2017. M.Sc. Dissertation. Universidade Tecnológica Federal do Paraná, Curitiba.
Jesus JMH. 2000. Estudo do adesivo poliuretano à base de mamona em madeira laminada colada (MLC). D.Sc. Thesis. Universidade de São Paulo, São Carlos.
Anjos e Silva SD, Andres A, Ueno B, Flores CA, Gomes CB, Pillon CN, Anthonisen D, Machado EB, Theisen G, Magnani M, Wrege MS, Aires RF. 2005. A cultura da Mamona na região de clima temperado: informações preliminares. 1st.ed. Pelotas: Embrapa Clima Temperado. pp.6-23.
Araújo LCR. 1992. Caracterização química e mecânica de poliuretanas elastoméricas baseadas em materiais oleoquímicos. M.Sc. dissertation. Universidade de São Paulo, São Carlos.
Wechsler A, Zaharia M, Crosky A, Jones H, Ramírez M, Ballerini A, Nuñez M, Sahajwalla V. 2013. Macadamia (Macadamia integrifolia) shell and castor (Rícinos communis) oil based sustainable particleboard: a comparison of its properties with conventional wood-based particleboard. Mater. Des. 50:117-123.
Maderuelo-Sanz R, García-Cobos FJ, Sánchez-Delgado FJ, Meneses-Rodríguez JM, Mota-López MI 2022. Mechanical and acoustical evaluation of bio-based composites made of cork granulates for acoustic ceiling tiles. Mater. Construcc. 72(347):e295.
Suoware TO, Edelugo SO, Ugwu BN, Amula E, Digitemie IE 2019. Development of flame retarded composite fibreboard for building applications using oil palm residue. Mater. Construcc. 69(335):e197.
Ezzahrae MF, Nacer A, Latifab E, Abdellah Z, Mohamed I, Jammoukh M. 2023. Thermal and mechanical properties of a High-density Polyethylene (HDPE) composite reinforced with wood flour. Mater. Today Proc. 72(7):3602-3608.
Stark NM, Cai Z. 2021. Wood-based composite materials: panel products, glued laminated timber, structural composite lumber, and wood-non wood composites. In: Wood handbook – wood as an engineering material. General Technical Report FPL-GTR-282. Madison: Department of Agriculture, Forest Service, Forest Products Laboratory. p.543.
Junxiong H, Zhinan W, Liping L, Chuigen G. 2023. Value-added utilization of corncob hydrolysis residues: preparation of reinforced wood-plastic composite with highly water resistance and decay resistance. Ind. Crops Prod. 195:116497.
Dharmaratne PD, Galabada H, Nilmini R, Jayasinghe R, Halwatura RU. 2021. Preliminary investigation of the suitability of coir fiber and thermoplastic waste as a construction material. Engineer. 54(4):65-74.
Chotikhun A, Kittijaruwattanna J, Arsyad WM, Salca E, Hadi Y, Hiziroglu S. 2022. Some properties of wood plastic composites made from rubberwood, recycled plastic and silica. Forests. 13(3):427.
Lopez YM, Paes JB, Gustave D, Gonçalves FG, Méndez FC, Nantet ACT. 2020. Production of wood-plastic composites using Cedrela odorata sawdust waste and recycled thermoplastics mixture from post-consumer products – A sustainable approach for cleaner production in Cuba. J. Clean. Prod. 244:118723.
Allaf RM, Albarahmieh E, Futian M. 2020. Preparation of sawdust-filled recycled-pet composites via solid state compounding. Processes 8(1):100.
Lopez YM, Paes J, Rodríguez E, Gustave D, Gonçalves FG. 2018. Wood particleboards reinforced with thermoplastics to improve th ickness swelling and mechanical properties. Cerne 24(4):369-378.
Rahman KS, Islam M, Rahman MM, Hannan MO, Dungani R, Khalil H. 2013.Flat-pressed wood plastic composites from sawdust and recycled polyethylene terephthalate (PET): physical and mechanical properties. SpringerPlus. 2:629.
Rahman KS, Islam MN, Ratul SB, Hasan ND, Musa S, Hannan MO. 2018. Properties of flat-pressed wood plastic composites as a function of particle size and mixing ratio. J. Wood Science. 64:279-286.
Campos PHS, Junior AJS, Souza, MV, Herradon MP, Libera VBL, Dezen LE, da Silva ÉV, e Silva AGBP, Rodrigues FR, Bispo RA, Cazella PHS, da Silva SAM, Christoforo AL 2023. Evaluation and production of high-strength wood composite panels with polyethylene terephthalate (PET). BioResources. 18(4):8528-8535.
Cazella PHS, Souza MV, Rodrigues FR, Silva SAM, Bispo RA, Araujo V, Christoforo AL. 2024. Polyethylene terephthalate (PET) as a recycled raw material for particleboards produced from Pinus wood and biopolymer resin. J. Clean. Prod. 447:141460.
Azevedo EC 2009. Efeito da radiação nas propriedades mecânicas do adesivo de poliuretano derivado de óleo de mamona. D.Sc. Thesis. Universidade Federal do Paraná, Curitiba, 2009.
Fiorelli J, Bueno SB, Cabral MR. 2019. Assessment of multilayer particleboards produced with green coconut and sugarcane bagasse fibers. Constr. Build. Mater. 205:1-9.
Celestino VRB 2020. Estudo do comportamento físico e mecânico de painéis aglomerados fabricados com partículas de Tectona grandis e Corymbia citriodora. D.Sc. thesis. Universidade Estadual Paulista, Bauru.
Borysiuk M, Piasecki J, Polak M. 2020. Effect of wood particles drying on the properties of wood composites. Compos. B Eng. 182:107586.
Klímek P, Morávek T, Ráhel J, Stupavská M, Decky D, Král PI, Kúdela J, Wimmer R. 2016. Utilization of air-plasma treated waste polyethylene terephthalate particles as a raw material for particleboard production. Compos. B Eng. 90:188-194.
ABNT – Associação Brasileira de Normas Técnicas. 2003. NBR NM 248: Determinação da composição granulométrica de materiais particulados. Rio de Janeiro, 2003.
Trevisan CG. 2021. Painéis aglomerados homogêneos produzidos com partículas de pinus e seringueira e aglutinados com adesivo poliuretano derivado de óleo de mamona – avaliação das propriedades físicas e mecânicas. M.Sc. dissertation, Universidade Estadual Paulista, Ilha Solteira.
Bispo RA (2021). Produção e avaliação de painéis de partículas de fibra de coco, pínus e eucalipto aglutinadas com adesivo poliuretano derivado de óleo de mamona. M.Sc. dissertation, Universidade Estadual Paulista, Ilha Solteira.
ABNT – Associação Brasileira de Normas Técnicas. 2017. NBR 6458: Grãos de pedregulho retidos na peneira de abertura 4,8 mm - Determinação da massa específica, da massa específica aparente e da absorção de água. Rio de Janeiro, ABNT.
ABNT – Associação Brasileira de Normas Técnicas. 2016. NBR 6457: Preparação de amostras para ensaios de compactação, caracterização e determinação do teor de umidade. Rio de Janeiro, ABNT.
Silva RM. 2018. Granulometria e suas influências na produção de painéis aglomerados. Jornal de Materiais e Engenharia 9(1):30-38.
Buzo ALSC, Sugahara ES, Silva SAM, Morales EAM, Azambuja MA. 2019.Painéis de Pinus e bagaço de cana empregando-se dois adesivos para uso na construção civil. Ambiente Construído. 19:183-193.
Sugahara ES, Silva SAM, Buzo ALSC, Campos C, Morales E, Ferreira BS, Azambuja MDA, Lahr F, Christoforo AL. 2019. High-density particleboard made from agro-industrial waste and differente adhesives. Bioresources. 14(3):5162-5170.
ANSI – American National Standards Institute. 2016. ANSI A208.1: Particleboard. Washington, ANSI.
Trianoski R. 2010. Avaliação do potencial de espécies florestais alternativas, de rápido crescimento, para produção de painéis de madeira aglomerada. D.Sc. dissertation. Universidade Federal do Paraná, Curitiba.
Dotun AO, Adesoji AA, Oluwatimilehin AC. 2018. Physical and mechanical properties evaluation of particle board produced from saw dust and plastic waste. Int. J. Eng. Res. Afr. 40:1-8.
Santos JA, Oliveira MA, Lima PA. 2011. Influência de resíduo de madeira na produção de painéis aglomerados. Revista Brasileira de Engenharia de Materiais 13(3):200-210.
Gilio CG. 2020. Avaliação de painéis de maravalhas homogêneas empregando-se madeira de Hevea brasiliensis e Tectona grandis, aglutinadas com adesivo poliuretano derivado de óleo de mamona. M.Sc. dissertation. Universidade Estadual Paulista, Ilha Solteira.
Souza MV, Silva SAM, Cazella PHS, Rodrigues FR, Bonfim KS, Sanches AO, Araujo VA, Santos HF, Pinto EM, Christoforo AL, Aouada MRM, Aouada FA, Lahr FA. Particleboards manufactured from Tectona grandis wood waste with homogeneous and three-layer heterogeneous compositions for commercial purposes. BioResources. 17(3):5011-5020, 2022.
Souza MV, Silva SAM, Cazella PHS, Rodrigues FR, Carneiro TEB, Pinto EM, Martins AR, Aouada MRM, Christoforo AL. 2023. Painéis aglomerados com resíduo de Pinus caribaea var. caribaea com adesivo bicomponente sustentável. Ambiente Construído. 23(3):263-276.
Souza MV, Cazella PHS, Bispo RA, Herradon MP, Santos Junior AJ, Alves MLXFN, Chotolli DL, Aouada MRM, Christoforo AL, Silva SAM. 2025. Use of Eucalyptus urophylla waste as raw material in composite particleboards. Revista Maderas. Ciencia y Tecnología. 27: e1925.
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Consejo Superior de Investigaciones Científicas (CSIC)
This work is licensed under a Creative Commons Attribution 4.0 International License.
© CSIC. Manuscripts published in both the print and online versions of this journal are the property of the Consejo Superior de Investigaciones Científicas, and quoting this source is a requirement for any partial or full reproduction.
All contents of this electronic edition, except where otherwise noted, are distributed under a Creative Commons Attribution 4.0 International (CC BY 4.0) licence. You may read the basic information and the legal text of the licence. The indication of the CC BY 4.0 licence must be expressly stated in this way when necessary.
Self-archiving in repositories, personal webpages or similar, of any version other than the final version of the work produced by the publisher, is not allowed.