Analysis of the properties of concrete produced with solid waste from the washing of ready-mix concrete trucks

T.M. Oliveira; L.F.  Jochem; C.A. Casagrande; R.D. Sakata; C.E. Maduro de Campos; A. Matoski

doi:10.3989/mc.2026.416025

Autores/as

T.M. Oliveira Department of Civil Engineering, Federal University of Technology Paraná https://orcid.org/0000-0003-2042-0363
L.F. Jochem Department of Civil Engineering, Federal University of Technology Paraná https://orcid.org/0000-0001-6679-2897
C.A. Casagrande Department of Civil Engineering, Federal University of Technology Paraná https://orcid.org/0000-0002-4293-6574
R.D. Sakata Department of Civil Engineering, Federal University of Technology Paraná https://orcid.org/0000-0002-7022-3846
C.E. Maduro de Campos Laboratory of X-ray Diffraction, Federal University of Santa Catarina https://orcid.org/0000-0001-5475-5116
A. Matoski Department of Civil Engineering, Federal University of Technology Paraná https://orcid.org/0000-0001-5503-4943

DOI:

https://doi.org/10.3989/mc.2026.416025

Palabras clave:

Hormigón, Lavado, Lodo residual de hormigón, Resistencia mecánica

Resumen

Las plantas mezcladoras de hormigón generan diversos tipos de residuos, incluidos los lodos residuales del lavado de camiones de hormigón premezclado. Este estudio tuvo como objetivo analizar las propiedades mecánicas del hormigón producido con la sustitución parcial (10%, 20% y 30%) del ligante por los residuos sólidos generados por el lavado de camiones de hormigón premezclado. Se caracterizaron física y químicamente los residuos y se evaluó su actividad puzolánica. Se realizaron ensayos para analizar el asentamiento y la densidad del hormigón en estado fresco, así como la resistencia a la compresión, la absorción de agua por inmersión, el índice de vacíos y la densidad del hormigón en estado endurecido. Se concluyó que la sustitución de hasta un 20% del ligante con residuos no comprometió significativamente las propiedades mecánicas, destacando la reducción en el consumo de cemento, lo que aportó ventajas en términos de sostenibilidad. Además, el análisis químico indicó que la presencia de fases como C-S-H y portlandita en los residuos podría influir positivamente en las propiedades del hormigón.

Descargas

Los datos de descargas todavía no están disponibles.

Citas

Martins JV, Aguilar MTP, Garcia DCS, dos Santos WJ. 2022. Management and characterization of concrete wastes from concrete batching plants in Belo Horizonte – Brazil. J. Mater. Res. Technol. 20(1157-1171).

Tsimas S, Zervaki M. 2011. Reuse of waste water from ready-mixed concrete plants. Manag. Environ. Qual. Int. J. 22(1):7-17.

Silva DOF da. 2016. Reaproveitamento de lamas residuais do processo de fabricação do concreto [Dissertação (Mestrado)], Universidade de São Paulo. São Paulo.

Malaguti V dos S, Mymrin VA, Matoski A. 2017. Reúso de água e resíduos de lavagem de caminhões betoneiras: análise do efeito na resistência à compressão em novos concretos. Matéria. 22(4):e-11885.

Chen X, Wu J, Ning Y, Zhang W. 2022. Experimental study on the effect of wastewater and waste slurry of mixing plant on mechanical properties and microstructure of concrete. J. Build. Eng. 52:104307.

Oliveira LJC, Soares MCB, Quaresma WMG, Adorno ALC. 2020. Gestão de resíduos: uma análise sobre os impactos da geração de rejeitos na construção civil. Braz. J. Dev. 6(5):24447-24462.

Ribeiro D, De Moura LS, Pirote NSS. 2016. Sustentabilidade: Formas de Reaproveitar os Resíduos da Construção Civil. Rev. Ciênc. Gerenc. 20(31):41-45.

Yang KH, Chung HS, Ashour AF. 2008. Influence of Type and Replacement Level of Recycled Aggregates on Concrete Properties. ACI Mater. J. 105(3):289-296.

Associação Brasileira de Normas Técnicas. 2003. NBR NM 248: Agregados - Determinação da composição granulométrica, ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. NBR NM 52: Agregado miúdo – Determinação de massa específica e massa específica aparente. Rio de Janeiro; 2009. Report.

Associação Brasileira de Normas Técnicas. 2009. NBR NM 53: Agregado graúdo - Determinação de massa específica, massa específica aparente e absorção de água, ABNT. Rio de Janeiro.

AAssociação Brasileira de Normas Técnicas. 2006. NBR NM 45: Agregados - Determinação de massa unitária e do volume de vazios, ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. 2021. NBR 16972: Agregados - Determinação de massa unitária e do índice de vazios, ABNT. Rio de Janeiro.

Snellings R, Salze A, Scrivener KL. 2014. Use of X-ray diffraction to quantify amorphous supplementary cementitious materials in anhydrous and hydrated blended cements. Cem. Concr. Res. 64:89-98.

Matos PR, Andrade Neto JS, Sakata RD, Kirchheim AP, Rodríguez ED, Campos CEM. 2022. Strategies for XRD quantitative phase analysis of ordinary and blended Portland cements. Cem. Concr. Compos. 131:104571.

Bergold ST, Goetz-Neunhoeffer F, Neubauer J. 2013. Quantitative analysis of C–S–H in hydrating alite pastes by in-situ XRD. Cem. Concr. Res. 53:119-126.

Scarlett NVY, Madsen IC. 2006. Quantification of phases with partial or no known crystal structures. Powder Diffr. 21(4):278-284.

Associação Brasileira de Normas Técnicas. 2014. NBR 5752: Materiais pozolânicos – Determinação do índice de desempenho com cimento Portland aos 28 dias, Editorial ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. 2014. NBR 12653: Materiais pozolânicos – Requisitos, Editorial ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. 2015. NBR 8953: Concreto para fins estruturais – Classificação pela massa específica, por grupos de resistência e consistência, ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. 1996. NBR NM 67: Concreto – Determinação da consistência pelo abatimento do tronco de cone, ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. 2008. NBR 9833: Concreto fresco – Determinação da massa específica, do rendimento e do teor de ar pelo método gravimétrico, ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. 2018. NBR 5739: Concreto – Ensaio de compressão de corpos de prova cilíndricos, ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. 2011. NBR 7222: Concreto e argamassa – Determinação da resistência à tração por compressão diametral de corpos de prova cilíndricos, ABNT. Rio de Janeiro.

Associação Brasileira de Normas Técnicas. 2005. NBR 9778: Argamassas e concreto endurecidos – Determinação da absorção de água, índice de vazios e massa específica, ABNT. Rio de Janeiro.

Fonseca GC da. 2010. Adições minerais e as disposições normativas relativas à produção de concreto no Brasil: Uma abordagem epistêmica [dissertação], Universidade Federal de Minas Gerais. Belo Horizonte.

Oliveira FA de, Casagrande CA, Marinho ÉP, Jochem LF, Nóbrega ACV de. 2022. Blasted copper slag as artificial fines in ecofriendly concrete. Matéria (Rio J.). 27(1):e1338.

Martins JV, Garcia DCS, Aguilar MTP, dos Santos WJ. 2021. Influence of replacing Portland cement with three different concrete sludge wastes. Constr. Build. Mater. 303:124519.

Aruntaş HY, Nallı E, Kaplan G. 2022. Usage of ready-mixed concrete plant wastewater in concrete with superplasticizer: Effect on physico-mechanical properties. Constr. Build. Mater. 348:128641.

Damineli BL, Kemeid FM, Aguiar PS, John VM. 2010. Measuring the eco-efficiency of cement use. Cem. Concr. Compos. 32(8):555-562.

Wang Y, Liu Z, Wang Y, Li Q, Gong X, Zhao Y. 2022. Effect of recycled aggregate and supplementary cementitious material on mechanical properties and chloride permeability of concrete. J. Clean. Prod. 369:133322.

Santos HMM, Jochem LF, de Matos PR, Casagrande CA, Marinho ÉP, Szeląg M, et al. 2023. Porcelain Tile Polishing Residue in Concrete as an Additive or Replacement for Portland Cement. Appl. Sci. 13(5):2824.

Elyamany HE, Abd Elmoaty AEM, Mohamed B. 2014. Effect of filler types on physical, mechanical and microstructure of self compacting concrete and Flow-able concrete. Alexandria Eng. J. 53(2):295-307.

Casagrande CA, Roque JS, Jochem LF, Correa JN, Medeiros A. 2023. Copper slag in cementitious composites: A systematic review. J. Build. Eng. 78:107725.

Jochem LF, Rocha JC. 2021. Potential Use of the Prewetting of Recycled and Lightweight Aggregates to Improve Cement Pastes for Residue Solidification / Stabilization Systems with Chromium and Zinc. J. Mater. Civ. Eng. 33(8):1-15.

CCasagrande CA, Jochem LF, Repette WL, Hotza D. 2020. Evaluation of nano-TiO2 on properties of cementitious mortars. Matéria (Rio J.). 25(4):e12883.

Casagrande CA, Jochem LF, Repette WL. 2020. Analysis of the 3-Glycidoxypropyltrimethoxysilane (GPTMS) hydrolysis by infrared spectroscopy. Matéria (Rio J.). 25(3):e12811.

Scrivener KL, Nonat A. 2011. Hydration of cementitious materials, present and future. Cem. Concr. Res. 41(7):651-665.

Scrivener KL, Juilland P, Monteiro PJM. 2015. Advances in understanding hydration of Portland cement. Cem. Concr. Res. 78:38-56.